Characterization of hot workability of IN617B alloy using activation energy, Zener-Hollomon parameter and hot processing maps

被引:11
|
作者
Luo, Rui [1 ]
Zhou, Yiming [1 ]
Gao, Pei [2 ]
Liu, Tian [1 ,3 ]
Cao, Yu [4 ]
Ding, Hengnan [1 ]
Lin, Wei [1 ]
Liu, Qingtao [1 ]
Tian, Tian [5 ]
机构
[1] Jiangsu Univ, Sch Mat Sci & Engn, Zhenjiang 212013, Jiangsu, Peoples R China
[2] Jiangsu Yinhuan Precis Steel Tube Co Ltd, Yixing 214200, Jiangsu, Peoples R China
[3] Hokkaido Univ, Grad Sch Engn, Sapporo 0608628, Japan
[4] Chongqing Univ, Coll Mat Sci & Engn, Chongqing 400045, Peoples R China
[5] Jiangsu Univ, Analyt & Testing Ctr, Zhenjiang 212013, Jiangsu, Peoples R China
来源
JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T | 2023年 / 26卷
关键词
IN617B alloy; Activation energy (Q) map; Zener-Hollomon parameter (Z) map; Hot processing map; Dynamic recrystallization; mechanism; DEFORMATION-BEHAVIOR; MICROSTRUCTURE EVOLUTION; WORKING BEHAVIOR; RECRYSTALLIZATION; SUPERALLOY;
D O I
10.1016/j.jmrt.2023.08.259
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
In order to predict the hot workability of the material more accurately, this paper takes the hot deformation of IN617B as the example. The activation energy (Q) map, Zener-Hollomon parameter (Z) map, and hot processing map were established based on the hot compression tests conducted at 950-1200 & DEG;C and 0.01-5 s-1. It was found that the area with high power dissipation values (denoted by h) in the hot processing map did not match the complete dynamic recrystallization (DRX) region completely. However, the microstructure corresponding to the high h area and low Z and Q area exhibited higher DRX. Therefore, the optimal hot processing region for this alloy was determined to be 1200 & DEG;C/0.1 s-1/0.8. Under this parameter, the DRX mechanism of IN617B alloy was dominated by discontinuous dynamic recrystallization (DDRX), supplemented by small amounts of continuous dynamic recrystallization (CDRX) and twinning dynamic recrystallization (TDRX).& COPY; 2023 The Author(s). Published by Elsevier B.V. This is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/).
引用
收藏
页码:5141 / 5150
页数:10
相关论文
共 50 条
  • [21] Hot workability integrating processing and activation energy maps of Inconel 740 superalloy
    Wang, Mingjia
    Wang, Wenrui
    Liu, Zhongli
    Sun, Chaoyang
    Qian, Lingyun
    MATERIALS TODAY COMMUNICATIONS, 2018, 14 : 188 - 198
  • [22] Characterization of Hot Workability of 5052 Aluminum Alloy Based on Activation Energy-Processing Map
    Zhou, Peng
    Deng, Lei
    Zhang, Mao
    Gong, Pan
    Wang, Xin-yun
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2019, 28 (10) : 6209 - 6218
  • [23] Characterization of Hot Workability of 5052 Aluminum Alloy Based on Activation Energy-Processing Map
    Peng Zhou
    Lei Deng
    Mao Zhang
    Pan Gong
    Xin-yun Wang
    Journal of Materials Engineering and Performance, 2019, 28 : 6209 - 6218
  • [24] Evaluation of Hot Workability of Nickel-Based Superalloy Using Activation Energy Map and Processing Maps
    Lypchanskyi, Oleksandr
    sleboda, Tomasz
    Zygula, Krystian
    Lukaszek-Solek, Aneta
    Wojtaszek, Marek
    MATERIALS, 2020, 13 (16)
  • [25] Characterization of hot workability in AA 7050 aluminum alloy using activation energy and 3-D processing map
    Wang, S.
    Hou, L. G.
    Luo, J. R.
    Zhang, J. S.
    Zhuang, L. Z.
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2015, 225 : 110 - 121
  • [26] OPTIMIZATION OF HOT WORKABILITY OF AN AL-MG-SI ALLOY USING PROCESSING MAPS
    SARKAR, J
    PRASAD, YVRK
    SURAPPA, MK
    JOURNAL OF MATERIALS SCIENCE, 1995, 30 (11) : 2843 - 2848
  • [27] Processing maps for hot deformation of the extruded 7075 aluminum alloy bar: Anisotropy of hot workability
    Yang, Yongbiao
    Xie, ZhiPing
    Zhang, Zhimin
    Li, Xubin
    Wang, Qiang
    Zhang, Yanhui
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2014, 615 : 183 - 190
  • [28] Characterization of Hot Workability for a Near Alpha Titanium Alloy by Integrating Processing Maps and Constitutive Relationship
    Zhou, Dadi
    Zeng, Weidong
    Xu, Jianwei
    Chen, Wei
    Wang, Simin
    ADVANCED ENGINEERING MATERIALS, 2019, 21 (07)
  • [29] Quantitative description of the flow-stress dependence of aluminum alloys at the stage of steady flow upon hot deformation on the Zener-Hollomon parameter
    Churyumov, A. Yu.
    Teleshov, V. V.
    PHYSICS OF METALS AND METALLOGRAPHY, 2017, 118 (09): : 905 - 912
  • [30] Relating grain size to the Zener-Hollomon parameter for twin-roll-cast AZ31B alloy refined by friction stir processing
    Ammouri, A. H.
    Kridli, G.
    Ayoub, G.
    Hamade, R. F.
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2015, 222 : 301 - 306