Effect of Temperature on Hard TiB2-Al2O3-Ti Coatings Deposited Using Electron Beam Physical Vapor Deposition

被引：1

作者：

Ali, Ajaz ^{[1
]}

AhmadnAff, Sheikh Nazir ^{[1
]}

机构：

[1] Natl Inst Technol, Dept Mech Engn, Srinagar 190006, Jammu & Kashmir, India

来源：

JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE | 2023年 / 32卷 / 10期

关键词：

Al2O3; coatings; nanoindentation; temperature; thin-film; TiB2; tribology; THERMAL BARRIER COATINGS; SUBSTRATE ROTATION; MECHANICAL-PROPERTIES; TEXTURE EVOLUTION; MICROSTRUCTURE; SURFACE; STABILITY; BEHAVIOR; MODULUS; LOAD;

D O I：

10.1007/s11665-022-07414-y

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

High-speed steel surfaces were coated with TiB2-Al2O3-(Ti 20%) thin film coatings of 4.9796 and 3.9036 mu m thickness, deposited using electron beam physical vapor deposition at 400 and 500 degrees C temperatures, respectively. Surface profilometer and 3D profilometer with AFM were used to analyze the coatings' thickness and surface roughness of the samples. Nanotribometer tests were used to evaluate thin film coatings' wear and friction behavior at varied loads of 0.5, 1, 1.5, and 2 N. Nanoindentation, FESEM, EDS, Raman Spectroscopy, and XRD were used to characterize the thin films. According to the findings, the nano-mechanical and nano-tribological behavior of the coating alters at different temperatures. The coating deposition which was done at low temperature of 400 degrees C performed better than the coating deposited high temperature of 500 degrees C.

引用

页码：4604 / 4625

页数：22

共 50 条

[21] Mechanical and tribological behavior of TiB2/Al2O3 coating on high-speed steel using electron beam deposition
Ali, Ajaz
Ahmad, Sheikh Nazir
TRIBOLOGY INTERNATIONAL, 2022, 174
[22] Research of Nd2O3 and Yb2O3 co-doped YSZ thermal barrier coatings produced by electron beam physical vapor deposition
Wei, Qiu-Li
Guo, Hong-Bo
Gong, Sheng-Kai
Hangkong Xuebao/Acta Aeronautica et Astronautica Sinica, 2007, 28 (SUPPL.): : 163 - 167
[23] Microstructures of Y2O3-stabilized ZrO2 electron beam-physical vapor deposition coatings on Ni-base superalloys
Unal, Ozer, 1600, American Ceramic Soc, Westerville, OH, United States (77):
[24] An Approach to Synthesize Thick α- and γ-Al2O3 Coatings by High-Speed Physical Vapor Deposition
Bobzin, Kirsten
Kalscheuer, Christian
Aghdam, Parisa Hassanzadegan
ADVANCED ENGINEERING MATERIALS, 2023, 25 (04)
[25] Microstructure and thermal cycling behavior of CeO2 coatings deposited by the electron beam physical vapor technique
Huang, Jianping
Song, Guangping
Lv, Hongzhen
Li, Yuxin
Sun, Yue
He, Xiaodong
Zhang, Sam
Fu, Yongqing
Du, Shanyi
Li, Yibin
THIN SOLID FILMS, 2013, 544 : 270 - 275
[26] PHYSICAL VAPOR-DEPOSITION OF TIN HARD COATINGS WITH ADDITIONAL ELECTRON-BEAM HEAT-TREATMENT
SCHULZ, A
STOCK, HR
MAYR, P
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1991, 140 (1-2): : 639 - 646
[27] Crystallinity of Al2O3 films deposited by metalorganic chemical vapor deposition
Pradhan, SK
Reucroft, PJ
Ko, YK
SURFACE & COATINGS TECHNOLOGY, 2004, 176 (03): : 382 - 384
[28] High Rate Deposition of Al2O3 Coatings Reactively Sputter Deposited
Mercs, David
Petitot, Christian
Duranteau, Audrey
Demange, Valerie
Coddet, Christian
PLASMA PROCESSES AND POLYMERS, 2007, 4 : S175 - S180
[29] Crystallographic texture evolution in ZrO2-Y2O3 layers produced by electron beam physical vapor deposition
Wada, K
Yamaguchi, N
Matsubara, H
SURFACE & COATINGS TECHNOLOGY, 2004, 184 (01): : 55 - 62
[30] MICROSTRUCTURES OF Y2O3-STABILIZED ZRO2 ELECTRON-BEAM PHYSICAL VAPOR-DEPOSITION COATINGS ON NI-BASE SUPERALLOYS
UNAL, O
MITCHELL, TE
HEUER, AH
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1994, 77 (04) : 984 - 992

← 1 2 3 4 5 →