Effect of Temperature on Hard TiB2-Al2O3-Ti Coatings Deposited Using Electron Beam Physical Vapor Deposition

被引：1
|
作者：
Ali, Ajaz [1 ]
AhmadnAff, Sheikh Nazir [1 ]
机构：
[1] Natl Inst Technol, Dept Mech Engn, Srinagar 190006, Jammu & Kashmir, India
来源：
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE | 2023年 / 32卷 / 10期
关键词：
Al2O3; coatings; nanoindentation; temperature; thin-film; TiB2; tribology; THERMAL BARRIER COATINGS; SUBSTRATE ROTATION; MECHANICAL-PROPERTIES; TEXTURE EVOLUTION; MICROSTRUCTURE; SURFACE; STABILITY; BEHAVIOR; MODULUS; LOAD;
D O I：
10.1007/s11665-022-07414-y
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
High-speed steel surfaces were coated with TiB2-Al2O3-(Ti 20%) thin film coatings of 4.9796 and 3.9036 mu m thickness, deposited using electron beam physical vapor deposition at 400 and 500 degrees C temperatures, respectively. Surface profilometer and 3D profilometer with AFM were used to analyze the coatings' thickness and surface roughness of the samples. Nanotribometer tests were used to evaluate thin film coatings' wear and friction behavior at varied loads of 0.5, 1, 1.5, and 2 N. Nanoindentation, FESEM, EDS, Raman Spectroscopy, and XRD were used to characterize the thin films. According to the findings, the nano-mechanical and nano-tribological behavior of the coating alters at different temperatures. The coating deposition which was done at low temperature of 400 degrees C performed better than the coating deposited high temperature of 500 degrees C.
引用
收藏
页码：4604 / 4625
页数：22
相关论文
共 50 条
  • [1] Effect of Temperature on Hard TiB2-Al2O3-Ti Coatings Deposited Using Electron Beam Physical Vapor Deposition
    Ajaz Ali
    Sheikh Nazir Ahmad
    Journal of Materials Engineering and Performance, 2023, 32 : 4604 - 4625
  • [2] Fracture Properties of α- and κ-Al2O3 Hard Coatings Deposited by Chemical Vapor Deposition
    Konstantiniuk, Fabian
    Tkadletz, Michael
    Czettl, Christoph
    Schalk, Nina
    COATINGS, 2021, 11 (11)
  • [3] Synthesis and characterization of multilayered TiC/TiB2 coatings deposited by ion beam assisted, electron beam-physical vapor deposition (EB-PVD)
    Wolfe, DE
    Singh, J
    Narasimhan, K
    SURFACE & COATINGS TECHNOLOGY, 2003, 165 (01): : 8 - 25
  • [4] Effect of physical vapor deposited Al2O3 film on TGO growth in YSZ/CoNiCrAlY coatings
    Li, Yanjun
    Xie, Youtao
    Huang, Liping
    Liu, Xuanyong
    Zheng, Xuebin
    CERAMICS INTERNATIONAL, 2012, 38 (06) : 5113 - 5121
  • [5] Nanoindentation of chemical-vapor deposited Al2O3 hard coatings at elevated temperatures
    de Figueiredo, Marisa Rebelo
    Abad, Manuel D.
    Harris, Adrian J.
    Czettl, Christoph
    Mitterer, Christian
    Hosemann, Peter
    THIN SOLID FILMS, 2015, 578 : 20 - 24
  • [6] Corrosion protection ability of Al2O3 coatings deposited with ion beam assisted deposition
    Emmerich, R
    Enders, B
    Martin, H
    Stippich, F
    Wolf, GK
    Andersen, PE
    Kudelha, J
    Lukac, P
    Hasuyama, H
    Shima, Y
    SURFACE & COATINGS TECHNOLOGY, 1997, 89 (1-2): : 47 - 51
  • [7] Corrosion protection ability of Al2O3 coatings deposited with ion beam assisted deposition
    Univ of Heidelberg, Heidelberg, Germany
    Surf Coat Technol, 1-2 (47-51):
  • [8] Preparation of Ti-Al alloy sheet by electron beam physical vapor deposition
    Ma Li
    He Xiao-Dong
    Sun Yue
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2007, 17 : S477 - S481
  • [9] Preparation of Ti-Al alloy sheet by electron beam physical vapor deposition
    马李
    赫晓东
    孙跃
    TransactionsofNonferrousMetalsSocietyofChina, 2007, (S1) : 477 - 481
  • [10] Plasma-enhanced chemical vapor deposition of TiB2 and TiBN hard coatings using BBr3
    Movassagh-Alanagh, Farid
    Abdollah-Zadeh, Amir
    Zolbin, Maryam Alizadeh
    Nemati, Narguess
    Aghababaei, Ramin
    TRIBOLOGY INTERNATIONAL, 2023, 179
12345