Rapid Microwave-Assisted Synthesis of ZnIn2S4 Nanosheets for Highly Efficient Photocatalytic Hydrogen Production

In this study, a facile and rapid microwave-assisted synthesis method was used to synthesize In2S3 nanosheets, ZnS nanosheets, and ZnIn2S4 nanosheets with sulfur vacancies. The two-dimensional semiconductor photocatalysts of ZnIn2S4 nanosheets were characterized by XRD, FESEM, BET, TEM, XPS, UV-vis diffuse reflectance, and PL spectroscopy. The ZnIn2S4 with sulfur vacancies exhibited an evident energy bandgap value of 2.82 eV, as determined by UV-visible diffuse reflectance spectroscopy, and its energy band diagram was obtained through the combination of XPS and energy bandgap values. ZnIn2S4 nanosheets exhibited about 33.3 and 16.6 times higher photocatalytic hydrogen production than In2S3 nanosheets and ZnS nanosheets, respectively, under visible-light irradiation. Various factors, including materials, sacrificial reagents, and pH values, were used to evaluate the influence of ZnIn2S4 nanosheets on photocatalytic hydrogen production. In addition, the ZnIn2S4 nanosheets revealed the highest photocatalytic hydrogen production from seawater, which was about 209.4 and 106.7 times higher than that of In2S3 nanosheets and ZnS nanosheets, respectively. The presence of sulfur vacancies in ZnIn2S4 nanosheets offers promising opportunities for developing highly efficient and stable photocatalysts for photocatalytic hydrogen production from seawater under visible-light irradiation.