Preparation of BaO-MgO-Al2O3-SiO2/Al2O3 glass-ceramic/ceramic LTCC substrate material for microwave application

被引：2

作者：

Mao, Haijun ^{[1
]}

Wang, Fenglin ^{[1
]}

Chen, Xingyu ^{[1
]}

Liu, Zhuofeng ^{[1
]}

Li, Wei ^{[1
]}

Zhang, Weijun ^{[1
]}

机构：

[1] Natl Univ Def Technol, Coll Aerosp Sci & Engn, Changsha 410073, Peoples R China

来源：

JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS | 2023年 / 34卷 / 04期

关键词：

CERAMICS; COMPOSITE; MICROSTRUCTURES; OPTIMIZATION;

D O I：

10.1007/s10854-022-09588-6

中图分类号：

TM [电工技术]; TN [电子技术、通信技术];

学科分类号：

0808 ; 0809 ;

摘要：

Through the avenue of adjusting the thermal properties of BaO-MgO-Al2O3-SiO2 (BMAS) glass-ceramic by changing the MgO/BaO ratio, a BMAS glass-ceramic with the MgO/BaO ratio of 1:2 has been obtained, which shows satisfactory softening and crystalline behavior. Then, this BMAS glass-ceramic is used to lower the sintering temperature of Al2O3 ceramic. After systematic research on the sintering and physical properties of BMAS /Al2O3 composite with different glass-ceramic content, we find that when the content of BMAS glass-ceramic is 50%, the composite presents adorable comprehensive properties: dielectric constant of 5.40 @ similar to 10 GHz, dielectric loss of 1.91 x 10(- 3) @ similar to 10 GHz and bending strength of 143 MPa, meeting the requirement of LTCC substrate material for microwave application.

引用

页数：12

共 50 条

[1] Preparation of BaO–MgO–Al2O3–SiO2/Al2O3 glass-ceramic/ceramic LTCC substrate material for microwave application
Haijun Mao
Fenglin Wang
Xingyu Chen
Zhuofeng Liu
Wei Li
Weijun Zhang
Journal of Materials Science: Materials in Electronics, 2023, 34
[2] Design of a BaO–Al2O3–SiO2–B2O3 glass-ceramic for microwave LTCC substrate material based on glass-ceramic + ceramic composite
Haijun Mao
Fenglin Wang
Xuelian Zhu
Xingyu Chen
Wei Li
Weijun Zhang
Journal of Materials Science: Materials in Electronics, 2022, 33 : 24834 - 24844
[3] Design of a BaO-Al2O3-SiO2-B2O3 glass-ceramic for microwave LTCC substrate material based on glass-ceramic plus ceramic composite
Mao, Haijun
Wang, Fenglin
Zhu, Xuelian
Chen, Xingyu
Li, Wei
Zhang, Weijun
JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2022, 33 (32) : 24834 - 24844
[4] Laser joining of Al2O3 liners with Al2O3-MgO-SiO2 glass-ceramic fillers
Luo, Bowei
Jiang, Shenglin
Zhu, Weiwei
Hu, Youyou
Qin, Yingxiong
Tang, Xiahui
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2018, 260 : 48 - 56
[5] Preparation and properties of Li2O-BaO-Al2-O3-SiO2 glass-ceramic materials
Khater, Gamal A.
Idris, Maher H.
PROCESSING AND APPLICATION OF CERAMICS, 2014, 8 (04) : 203 - 210
[6] Preparation of a CaO-Al2O3-B2O3-SiO2 glass/Al2O3 LTCC substrate material with high flexural strength for microwave application
Zhu, Xuelian
Mao, Haijun
Wang, Fenglin
Liang, Riran
Chen, Xingyu
Liu, Zhuofeng
Li, Wei
Zhang, Weijun
JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2023, 34 (13)
[7] Preparation of a CaO–Al2O3–B2O3–SiO2 glass/Al2O3 LTCC substrate material with high flexural strength for microwave application
Xuelian Zhu
Haijun Mao
Fenglin Wang
Riran Liang
Xingyu Chen
Zhuofeng Liu
Wei Li
Weijun Zhang
Journal of Materials Science: Materials in Electronics, 2023, 34
[8] Dielectric properties of MgO-Al2O3-SiO2 glass-ceramic
Zhang, Qilong
Yang, Hui
Sun, Huiping
Huang, Wei
Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2005, 34 (SUPPL. 1 PART 2): : 680 - 681
[9] Crystallization and microwave dielectric properties of CaO-B2O3-SiO2 2 O 3-SiO 2 glass-ceramic/Al2O3 2 O 3 for LTCC applications
Xiong, Zilong
Tan, Feihu
Zhang, Yi
Wang, Qing
Yu, Hongyu
MATERIALS TODAY COMMUNICATIONS, 2024, 40
[10] Li2O-MgO-B2O3-Al2O3-SiO2 GLASS-CERAMIC FOR DENTAL VENEERING APPLICATION
Cherdtham, Narawat
Mongkolkachit, Charusporn
Wasanapiarnpong, Thanakorn
SURANAREE JOURNAL OF SCIENCE AND TECHNOLOGY, 2014, 21 (02): : 97 - 103

← 1 2 3 4 5 →