Intermediate annealing and strong cube texture of Ni-5at.%W alloy thin substrates for YBCO coated conductors

In this work, a series of studies have been carried out on ultra-thin Ni-5at%W (Ni5W) alloy substrates used for the coated conductors. The ultra-thin Ni5W alloy substrate can be fabricated for the large square REBCO film with a size of over 40 mm x 40 mm, which is normally used in scenarios to support a magnetic field in a specific area. To obtain a stronger recrystallized cubic texture, the intermediate annealing was added to optimize the rolling texture during the rolling process of the Ni5W alloy substrate. A typical copper-type rolling texture was obtained in the substrate which intermediate annealed at 96.25%, and the cube texture reached 97.6% after annealing recrystallization. Moreover, The deformation and recrystallization of 40 & mu;m thick Ni-5at%W (Ni5W) alloy thin substrates were investigated by the quasi-in situ method. The fabrication of ultra-thin Ni5W substrates increases the potential of miniaturizing lightweight coated conductors, which helps to further promote and accelerate the manufacturing process of the entire coated conductor strip.