Corrosion cracking behavior of reinforced concrete under freeze-thaw cycles

被引：31
|
作者：
Liu, Xiguang [1 ,2 ]
Yan, Ziwei [2 ]
Wang, Dongjing [3 ]
Zhao, Rong [2 ,4 ]
Niu, Ditao [1 ,2 ]
Wang, Yan [5 ]
机构：
[1] Xian Univ Architecture & Technol, State Key Lab Green Bldg Western China, 13 Yanta Rd, Xian 710055, Peoples R China
[2] Xian Univ Architecture & Technol, Coll Civil Engn, 13 Yanta Rd, Xian 710055, Peoples R China
[3] China JiKan Res Inst Engn Invest & Design Co Ltd, 51 Xianning Rd, Xian 710043, Peoples R China
[4] Beijing Glory PKPM Technol Co Ltd, 30 North Third Ring Rd East, Beijing 100013, Peoples R China
[5] Xian Univ Architecture & Technol, Coll Mat & Engn, 13 Yanta Rd, Xian 710055, Peoples R China
来源：
JOURNAL OF BUILDING ENGINEERING | 2023年 / 64卷
基金：
中国国家自然科学基金;
关键词：
Reinforced concrete; Freeze-thaw cycles; Corrosion cracking; Damaged layer thickness; TIME; SURFACE;
D O I：
10.1016/j.jobe.2022.105610
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
This paper presents an experimental and theoretical study on the corrosion cracking behavior of reinforced concrete under freeze-thaw cycles. Accelerated corrosion tests were carried out on reinforced concrete specimens subjected to freeze-thaw cycles. The test results of Digital Image Correlation (DIC) showed that the cracking positions on the concrete surface were randomly distributed. The critical corrosion ratio of reinforcing bars decreased with increasing freeze-thaw cycles. The reinforcing bar critical corrosion ratio at cover cracking under freeze-thaw environ-ment was established with the thick-walled double cylinder theory, and was in acceptable with experimental results.
引用
收藏
页数：14
相关论文
共 50 条
  • [21] Experiments of persistent loading reinforced concrete beams with freeze-thaw cycles
    Diao, Bo
    Sun, Yang
    Ye, Ying-Hua
    Zhongnan Daxue Xuebao (Ziran Kexue Ban)/Journal of Central South University (Science and Technology), 2011, 42 (03): : 785 - 790
  • [22] Evolution and Characterization of Damage of Concrete under Freeze-thaw Cycles
    王玲
    CAO Yin
    WANG Zhendi
    DU Peng
    Journal of Wuhan University of Technology(Materials Science Edition), 2013, (04) : 710 - 714
  • [23] Evolution and characterization of damage of concrete under freeze-thaw cycles
    Wang Ling
    Cao Yin
    Wang Zhendi
    Du Peng
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2013, 28 (04): : 710 - 714
  • [24] Seismic performance of reinforced concrete columns after freeze-thaw cycles
    Xu, Shanhua
    Li, Anbang
    Ji, Zengyang
    Wang, Yan
    CONSTRUCTION AND BUILDING MATERIALS, 2016, 102 : 861 - 871
  • [25] Flexural Behaviour of Reinforced Concrete Members Subjected to Freeze-Thaw Cycles
    Duan, An
    Jin, Weiliang
    FRONTIERS OF GREEN BUILDING, MATERIALS AND CIVIL ENGINEERING, PTS 1-8, 2011, 71-78 : 712 - 716
  • [26] Hysteretic Behavior of Eccentrically Loaded Reinforced Air-Entrained Concrete Columns under Combined Effects of Freeze-Thaw Cycles and Seawater Corrosion
    Wu, Jieqiong
    Zhang, Jian
    Diao, Bo
    Cheng, Shaohong
    Ye, Yinghua
    ADVANCES IN CIVIL ENGINEERING, 2018, 2018
  • [27] Dynamic Behavior of Geosynthetic-Reinforced Expansive Soil under Freeze-Thaw Cycles
    Zhongnian, Yang
    Liu, Xuesen
    Zhang, Liang
    Niu, Fujun
    Ling, Xianzhang
    Li, Guoyu
    Shi, Wei
    ADVANCES IN CIVIL ENGINEERING, 2021, 2021
  • [28] Fractal analysis of cracking in a clayey soil under freeze-thaw cycles
    Lu, Yang
    Liu, Sihong
    Weng, Liping
    Wang, Liujiang
    Li, Zhuo
    Xu, Lei
    ENGINEERING GEOLOGY, 2016, 208 : 93 - 99
  • [29] Bond Behavior of Steel Bars in Concrete Confined with Stirrups under Freeze-Thaw Cycles
    Liu, Guirong
    Dou, Xiaoxue
    Qu, Fulai
    Shang, Pengran
    Zhao, Shunbo
    MATERIALS, 2022, 15 (20)
  • [30] Compressive behavior of concrete under high strain rates after freeze-thaw cycles
    Chen, Xudong
    Chen, Chen
    Liu, Zhiheng
    Lu, Jun
    Fan, Xiangqian
    COMPUTERS AND CONCRETE, 2018, 21 (02): : 209 - 217
12345