Fluidity and Strength of Loess-Based Quick Consolidated Backfill Material with One High-Water Content

To study the flow and strength characteristics of loess-based backfill materials, orthogonal tests were used to design a cemented backfill material combining loess, high-water content materials, cement, and fly ash. By using the range, analysis of variance, and multi-variate regression analysis, influences of four key factors on the initial setting time, diffusivity, compressive strength, and shear strength of the backfill material were investigated. These four factors included the mass concentration of loess water (A), the content of high-water content materials (B), cement content (C), and content of fly ash (D). The results showed that the initial setting time, diffusivity, compressive strength, and shear strength of the backfill material were 13 similar to 33 min, 400 similar to 580 mm, 0.917-3.605 MPa, and 0.360-0.722 MPa, respectively, all distributed in wide ranges. For the initial setting time, the four factors were listed in descending order as A > D > B > C according to their influences; for diffusivity, the four factors were listed as A > B > C > D; for the compressive strength, the four factors were ranked as A > C > D > B; for the shear strength, the four factors were ranked such that A > C > D > B. With regard to the comprehensive index, the four factors were such that A > B > D > C. That is, the factors were listed in descending order as the mass concentration of loess water, cement content, the content of fly ash, and content of high-water content materials according to their significance in influencing characteristics of the loess-based backfill material. Comprehensive analysis indicated that the fluidity of the material was mainly influenced by the mass concentration of loess water, and the two were negatively correlated. The hydro-consolidation effect of materials with high-water contents accelerated material solidification. The strength of the backfill material was mainly influenced by the cement content while only slightly affected by contents of other materials. In this way, a prediction model for characteristic parameters, namely, fluidity and strength, of the loess-based backfill material under the action of various factors was established.