Effect of heat treatment on properties and interfacial compatibility of poplar veneer/polyethylene film composite plywood

被引：4
|
作者：
Zheng, Siqi [1 ]
Chen, Muyang [1 ]
Wu, Jiabiao [1 ]
Xu, Jianying [1 ]
机构：
[1] Cent South Univ Forestry & Technol, Coll Mat Sci & Engn, Changsha 410004, Hunan, Peoples R China
来源：
POLYMER TESTING | 2023年 / 122卷
关键词：
Poplar veneer; PE film; Heat treatment; Interfacial compatibility; SURFACE MODIFICATION; WOOD; DEGRADATION; DURABILITY; VENEER;
D O I：
10.1016/j.polymertesting.2023.108006
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
This study aimed to enhance the properties and interfacial compatibility of poplar veneer/polyethylene (PE) film composite plywood using heat treatment by prolonging the hot-pressing time. The plywood was heat-treated (long time hot-pressed) at 160, 180, and 200 degrees C for 2 h. The results showed that after being heat-treated at 180 degrees C for 2 h, the shear strength of the plywood was effectively increased from 0.49 MPa to 0.94 MPa, which met the requirements of type I plywood according to the Chinese National Standard GB/T 9846-2015. The higher the treatment temperature, the better the water resistance and durability of the plywood. The Fourier transform infrared spectroscopy (FTIR) spectra indicated that the number of hydroxyl groups and carbonyl groups was reduced after heat treatment, thus decreasing the surface hydrophilicity of poplar veneer. The scanning electron microscopy (SEM) images showed that heat-treated plywood possessed more continuous and uniform glueline compared with untreated plywood.
引用
收藏
页数：8
相关论文
共 50 条
  • [21] Effect of Dipping Treatment on Flame Retardant Property of Poplar Plywood
    Zhu, Xiaodan
    Yang, Jianming
    Long, Kequan
    Yang, Shoulu
    Liu, Xiaomei
    Luo, Sha
    Chen, Xun
    Wu, Yiqiang
    2012 INTERNATIONAL CONFERENCE ON BIOBASE MATERIAL SCIENCE AND ENGINEERING (BMSE), 2012, : 112 - 116
  • [22] Heat transfer during pressing of 3d moulded veneer plywood composite materials
    Igaz R.
    Krišták L.
    Ružiak I.
    Réh R.
    Danihelová Z.
    Key Engineering Materials, 2016, 688 : 131 - 137
  • [23] Effect of heat treatment on some physical and mechanical properties of birch plywood
    Bekhta, Pavlo
    EUROPEAN JOURNAL OF WOOD AND WOOD PRODUCTS, 2020, 78 (04) : 683 - 691
  • [24] Effect of heat treatment on some physical and mechanical properties of birch plywood
    Pavlo Bekhta
    European Journal of Wood and Wood Products, 2020, 78 : 683 - 691
  • [25] THE EFFECT OF VENEER IMPREGNATION WITH A MIXTURE OF POTASSIUM CARBONATE AND UREA ON THE PROPERTIES OF MANUFACTURED PLYWOOD
    Kawalerczyk, Jakub
    Dziurka, Dorota
    Mirski, Radoslaw
    Grzeskowiak, Wojciech
    DREWNO, 2019, 62 (203): : 107 - 116
  • [26] Effect of Heat Treatment on Interfacial Compatibility of Mesophase Pitch - Carbon Fiber Binding
    Ouyang T.
    Chen Y.
    Jiang Z.
    Li G.
    Hunan Daxue Xuebao/Journal of Hunan University Natural Sciences, 2021, 48 (06): : 24 - 29
  • [27] Effect of surface treatment on mechanical properties of polyethylene composite
    Rochette, A
    Bousmina, M
    Lavoie, A
    Ajji, A
    JOURNAL OF COMPOSITE MATERIALS, 2002, 36 (08) : 925 - 940
  • [28] Micromechanical model of tensile properties of poplar fiber/polyethylene composite
    Sun H.
    Lv X.
    Guo C.
    Wang Q.
    Yuan N.
    Sun L.
    Fuhe Cailiao Xuebao/Acta Materiae Compositae Sinica, 2021, 38 (01): : 155 - 164
  • [29] The effect of Boric acid/Borax treatment on selected mechanical and combustion properties of poplar laminated veneer lumber
    Kurt, Ramazan
    Mengeloglu, Fatih
    WOOD RESEARCH, 2008, 53 (02) : 113 - 120
  • [30] Assessing the Tensile Shear Strength and Interfacial Bonding Mechanism of Poplar Plywood with High-density Polyethylene Films as Adhesive
    Chang, Liang
    Guo, Wenjing
    Tang, Qiheng
    BIORESOURCES, 2017, 12 (01): : 571 - 585
12345