A method to eliminate the cracking of Stellite 6+WC laser cladding layers using ultrasonic impact treatment

被引：6
|
作者：
Li, Yongjian [1 ]
Liu, Xiaoting [2 ]
Wang, Fang [3 ]
Gu, Heng [1 ]
Zhou, Wangfan [1 ]
Ren, Xudong [1 ]
机构：
[1] Jiangsu Univ, Sch Mech Engn, Zhenjiang 212013, Peoples R China
[2] Army Acad Armored Forces, Natl Key Lab Remfg, Beijing 100072, Peoples R China
[3] Zhenjiang Stomatol Hosp, Zhenjiang, Peoples R China
来源：
MATERIALS LETTERS | 2024年 / 355卷
基金：
中国国家自然科学基金;
关键词：
Ultrasonic impact; Ceramics; Microstructure; Stellite alloy; FATIGUE;
D O I：
10.1016/j.matlet.2023.135491
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Enhancing the wear resistance of coatings is a widely used technique that involves adding WC ceramic particles to Stellite alloy. Practical applications may be challenging due to the significant coating breaking that might result from the inclusion of WC ceramic particles. In this paper, the ultrasonic impact treatment (UIT) method was used to decrease the residual stress during the cladding process of WC reinforced Stellite 6 alloy coating, consequently reducing the coating's tendency to crack. The results showed that the cracking can be eliminated in the coating reinforced by 20 % WC ceramic particles utilizing UIT.
引用
收藏
页数：4
相关论文
共 50 条
  • [11] Microstructural features of consecutive layers of Stellite 6 deposited by laser cladding
    D'Oliveira, ASCM
    da Silva, PSCP
    Vilar, RMC
    SURFACE & COATINGS TECHNOLOGY, 2002, 153 (2-3): : 203 - 209
  • [12] Microstructure and Properties of the Stellite6/WC Composite Coatings Prepared by Laser Cladding
    Zhang H.
    Liu H.
    Ren C.
    Li Z.
    Hou S.
    Lasers in Manufacturing and Materials Processing, 2023, 10 (04): : 645 - 658
  • [13] Microstructure, microhardness and corrosion resistance of Stellite-6 coatings reinforced with WC particles using laser cladding
    Bartkowski, Dariusz
    Mlynarczak, Andrzej
    Piasecki, Adam
    Dudziak, Bartlomiej
    Goscianski, Marek
    Bartkowska, Aneta
    OPTICS AND LASER TECHNOLOGY, 2015, 68 : 191 - 201
  • [14] Research on the Microstructure and Properties of Stellite6/WC Composite Coatings via Laser Cladding
    Yang, Jianjun
    Peng, Hai
    Zhao, Kangwei
    Fan, Caihe
    Luo, Deng
    Wu, Qin
    Ou, Ling
    Yin, Shiyang
    Dong, Shiyun
    Wang, Qiangping
    Zhang, Zaiyu
    JOM, 2024, : 3769 - 3782
  • [15] Microstructure and tribological property of laser cladding Stellite 6 alloy by laser remelting and ultrasonic surface rolling
    Sun, Jiayu
    Zhang, Yingying
    Sun, Zhengyu
    Yu, Tianbiao
    Wang, Guofa
    SURFACE & COATINGS TECHNOLOGY, 2025, 495
  • [16] Microstructure and wear resistance of Stellite-6/WC MMC coatings produced by laser cladding using Yb:YAG disk laser
    Bartkowski, Dariusz
    Kinal, Grzegorz
    INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2016, 58 : 157 - 164
  • [17] Impact wear resistance of Stellite 6 hardfaced valve seats with laser cladding
    Chang, Shu-Shuo
    Wu, Hsieh-Chen
    Chen, Chun
    MATERIALS AND MANUFACTURING PROCESSES, 2008, 23 (07) : 708 - 713
  • [18] The effect of CeO2 on microstructure and properties of laser cladding stellite6/WC coating
    Lin, Qingcheng
    Guo, Chun
    Hong, Changhua
    Li, Wenqing
    Huang, Guangcan
    Zhang, Xinyu
    Qin, Chi
    METALLURGICAL RESEARCH & TECHNOLOGY, 2025, 122 (03)
  • [19] CO2 and Nd:YAG laser cladding using Stellite 6
    Jansson, A
    Ion, JC
    Kujanpää, V
    FIRST INTERNATIONAL SYMPOSIUM ON HIGH-POWER LASER MACROPROCESSING, 2003, 4831 : 475 - 480
  • [20] Effect of Preheating Temperature on Geometry and Mechanical Properties of Laser Cladding-Based Stellite 6/WC Coating
    Wu, Teng
    Shi, Wenqing
    Xie, Linyi
    Gong, Meimei
    Huang, Jiang
    Xie, Yuping
    He, Kuanfang
    MATERIALS, 2022, 15 (11)
12345