Adhesive Performance of Resin Cement to Glass-Ceramic and Polymer-Based Ceramic CAD/CAM Materials after Applying Self-Etching Ceramic Primer or Different Surface Treatments

Ensuring optimum bond strength during cementation is vital for restoration success, with the practicality of the process being crucial in clinical practice. This study analyzed the effect of a single-step self-etching ceramic primer (MEP) and various surface treatments on the microshear bond strength (mu SBS) between resin cement and glass-ceramic or polymer-based ceramic CAD/CAM materials. Specimens were fabricated from leucite-based glass-ceramic (LEU), lithium disilicate glass-ceramic (LDC), resin nanoceramic (RNC), and polymer infiltrated ceramic network (PICN) (n = 160). They were then classified based on the surface treatments (n = 10): control (no treatment); sandblasting with Al2O3 (AL); etching with hydrofluoric acid (HF); and MEP application. Scanning electron microscopy was used to evaluate the surface topography. mu SBS was measured after cementation and thermocycling procedures. Failure modes were examined with a stereomicroscope. Statistical analysis involved two-way analysis of variance and Tukey HSD tests with a significance level of 0.05. mu SBS was significantly influenced by both surface treatment and CAD/CAM material type. The most enhanced mu SBS values for each material, regarding the surface treatment, were: LEU and LDC, HF; RNC, AL; PICN, AL or HF. MEP significantly increased the mu SBS values of CAD/CAM materials except RNC, yet it did not yield the highest mu SBS values for any of them.