Influence of oxalic acid on the corrosion behavior of AZ91D magnesium alloy in deionized water

被引：6

作者：

Liu, Sisi ^{[1
]}

Huang, Hualiang ^{[1
]}

Huang, Gangliang ^{[2
]}

Qu, June ^{[3
]}

机构：

[1] Wuhan Inst Technol, Sch Chem & Environm Engn, Key Lab Green Chem Proc, Key Lab Novel Reactor & Green Chem Technol Hubei P, Wuhan 430074, Peoples R China

[2] Chongqing Normal Univ, Key Lab Carbohydrate Sci & Engn, Chongqing 401331, Peoples R China

[3] Hubei Univ, Key Lab Green Preparat & Applicat Funct Mat, Minist Educ, Wuhan 430062, Peoples R China

来源：

VACUUM | 2023年 / 215卷

基金：

中国国家自然科学基金;

关键词：

Magnesium alloy; Oxalic acid; Corrosion; Hydrogen evolution; ETHYLENE-GLYCOL; SURFACE-CHEMISTRY; IMPEDANCE; AZ31; MECHANISM; AMBIENT; XPS;

D O I：

10.1016/j.vacuum.2023.112351

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Due to its light weight, Mg alloy can be applied to automotive engines and cooling systems to reduce vehicle weight, energy consumption and exhaust pollution. However, ethylene glycol-type coolants can be oxidized into oxalic acid, glyoxylic acid and other substances at high temperature, which can cause the damage of Mg alloy. In this paper, electrochemical methods, hydrogen evolution and surface analysis methods were used to study the influence of oxalic acid on the corrosion behavior of AZ91D magnesium alloy in deionized water. The results indicated that the oxalic acid accelerated the corrosion of Mg alloy, and its corrosion rate increased with the concentration of oxalic acid. However, interestingly, the corrosion rate of Mg alloy in oxalic acid solution slowed as the immersed time lengthened, which could be related to the accumulation of corrosion products and the consumption of hydrogen ions. The main corrosion product of the corrosion of Mg alloy in oxalic acid solution was composed of magnesium oxalate.

引用

页数：11

共 50 条

[1] Corrosion behavior of AZ91D magnesium alloy in distilled water
Huang, Hualiang
Yang, Wenlu
ARABIAN JOURNAL OF CHEMISTRY, 2020, 13 (07) : 6044 - 6055
[2] Corrosion behavior of AZ91D magnesium alloy in city atmosphere
Lin, C
Li, XG
Li, M
Wang, FP
ACTA METALLURGICA SINICA, 2004, 40 (02) : 191 - 196
[3] Galvanic corrosion behavior between AZ91D magnesium alloy and copper in distilled water
Yang, Wenlu
Liu, Zeqi
Huang, Hualiang
CORROSION SCIENCE, 2021, 188 (188)
[4] Corrosion behavior of AZ91D magnesium alloy in sodium sulfate solution
Chen, J.
Wang, J.
Han, E.
Dong, J.
Ke, W.
MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2006, 57 (10): : 789 - 793
[5] Corrosion behavior of microarc oxidation film on AZ91D magnesium alloy
Zhi Qing
Gao Jin
Dong Chaofang
Li Xiaogang
ACTA METALLURGICA SINICA, 2008, 44 (08) : 986 - 990
[6] Influence of Zeolite Coating on the Corrosion Resistance of AZ91D Magnesium Alloy
Banerjee, P. Chakraborty
Woo, Ren Ping
Grayson, Sam Matthew
Majumder, Amrita
Raman, R. K. Singh
MATERIALS, 2014, 7 (08) : 6092 - 6104
[7] Influence of pH on Stress Corrosion Behavior of Thixoformed and Metal Mould AZ91D Magnesium Alloy
Institute of Materials Science and Engineering, Lanzhou University of Technology, State Key Laboratory of New Nonferrous Metal Materials, Lanzhou 730050, China
Zhuzao, 2006, 8 (835-838):
[8] Influence of Surface Nanocrystallization on Aluminizing Behavior of AZ91D Magnesium Alloy
Zhang Conghui
Song Guodong
Wang Jing
Zhao Xu
RARE METAL MATERIALS AND ENGINEERING, 2020, 49 (02) : 447 - 453
[9] Influence of Surface Nanocrystallization on Aluminizing Behavior of AZ91D Magnesium Alloy
Zhang, Conghui
Song, Guodong
Wang, Jing
Zhao, Xu
Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2020, 49 (02): : 447 - 453
[10] Effect of Heat Treatment on Microstructure and Corrosion Behavior of Az91d Magnesium Alloy
Lih, Chye T.
Zamzuri, M. Z. M.
Norbahiyah, S.
Ismail, K. A.
Derman, M. N. B.
Illias, S.
ADVANCED MATERIALS RESEARCH III, 2013, 685 : 102 - +

← 1 2 3 4 5 →