The Effect of Secondary Aluminum Ash on the Properties of Reactive Powder Concrete

Secondary aluminum ash is a kind of common solid waste which will pollute the environment without any treatment. In this study, the influence of secondary aluminum ash on the rheological properties and the initial setting time of fresh reactive powder concrete (RPC) are researched. Meanwhile, the mechanical properties and the drying shrinkage rates of RPC with the secondary aluminum ash are determined. The electrical parameters of RPC with the secondary aluminum ash are measured. Scanning electron microscopy is obtained to reflect the internal structure of RPC. Results show that the addition of secondary aluminum ash can lead to decreasing the fluidity and increase the yield shear stress of fresh RPC paste by varying rates of 16.1% and 58.3%, respectively. The addition of secondary aluminum ash can decrease the flexural and compressive strengths of RPC cured for 1 day by the decreasing rates of 0 similar to 18.7% and 0 similar to 19.3%. When the curing age is 28 days, the flexural and compressive strengths of RPC are increased by 0 similar to 9.1% and 0 similar to 19.1% with adding the secondary aluminum ash. The secondary aluminum ash can promote the condensation of RPC. The addition of the secondary aluminum ash can decrease the electrical resistance of RPC by an order of magnitude. The relationship between the electrical resistance and the electrical reactance fits the quadratic function equation. The electrical resistance of the pore solution increases in the form of a quadratic function with the mass ratio of the secondary aluminum ash. The dry shrinkage rates of RPC cured for 1 day and 28 days are decreased by 0 similar to 36.4% and 0 similar to 41.3% with the increasing dosages of secondary aluminum ash. As obtained from the microscopic testing results, the secondary aluminum ash can improve the compactness of hydration products.