Experimental study on supercritical phenomena of WO3 solubility in NaCl-H2O system

被引：0
|
作者：
龚庆杰
岑况
於崇文
机构：
[1] Institute of Mineral Resources, Chinese Academy of Geological Sciences, Beijing 100037, China , Beijing 100083, China , Beijing 100083, China
[2] China University of Geosciences,China University of Geosciences, China University of Geosciences Beijing 100083, China
来源：
ScienceinChina(SeriesD:EarthSciences) | 2003年 / 07期
关键词：
supercritical phenomenon; critical region; tungsten; solubility; tungsten deposit;
D O I：
暂无
中图分类号：
P59 [地球化学];
学科分类号：
070902 ;
摘要：
The solubility measurements of WO3 in NaCl-H2O system with 4.0% by weight salt were carried out to study the supercritical phenomena of solubility. These experiments were carried out using rapid-quench pressure vessels, with quantitative Na2WO42H2O, HCl, NaCl and H2O in Pt capsule to determine the solubility of WO3 from supersaturated solution. The pressure was kept at 34 MPa, which was near the critical pressure 31.4 MPa and the temperatures varied from 250℃ to 550℃. The experimental results indicate that the solubility of WO3 has the features of supercritical phenomenon in critical region and is sensitive to the change of system temperature and solvent density. The temperature and pressure in this experiment are close to those of ore-forming fluids in many tungsten deposits, so the features of supercritical geofluids can be helpful to investigating the ore-forming mechanism of tungsten deposit.
引用
收藏
页码：664 / 671
页数：8
相关论文
共 50 条
  • [21] Experimental study of the Na-in-cordierite thermometer at different fluid compositions (NaOH-H2O;: NaCl-H2O)
    Scola, M.
    Mirwald, P. W.
    Tropper, P.
    GEOCHIMICA ET COSMOCHIMICA ACTA, 2007, 71 (15) : A912 - A912
  • [22] Contribution to the system WO3/H2O IV Crystallography of hydrates WO2, 2H(2)O
    Buchholz, E
    ZEITSCHRIFT FUR ANORGANISCHE UND ALLGEMEINE CHEMIE, 1940, 244 (03): : 245 - 251
  • [23] Molecular simulations of dense hydrothermal NaCl-H2O solutions from subcritical to supercritical conditions
    Reagan, MT
    Harris, JG
    Tester, JW
    JOURNAL OF PHYSICAL CHEMISTRY B, 1999, 103 (37): : 7935 - 7941
  • [24] SOLUBILITY IN NACL-TETRAHYDROFURAN-H2O SYSTEM
    ZATSEPIN, IA
    KOMLEV, GA
    ZHURNAL NEORGANICHESKOI KHIMII, 1981, 26 (02): : 554 - 555
  • [25] Study on Phase Transition Process of NaCl-H2O and NaCl-KCl-H2O at Low Temperature with in Situ XRD
    Yang Hong-jun
    Chai Xiao-li
    Wang Min
    Li Bing
    SPECTROSCOPY AND SPECTRAL ANALYSIS, 2018, 38 (03) : 953 - 957
  • [26] Fe isotope fractionation during phase separation in the NaCl-H2O system: An experimental study with implications for seafloor hydrothermal vents
    Syverson, Drew D.
    Pester, Nicholas J.
    Craddock, Paul R.
    Seyfried, William E., Jr.
    EARTH AND PLANETARY SCIENCE LETTERS, 2014, 406 : 223 - 232
  • [27] Electrical conductivity of NaCl-H2O fluid in the crust
    Sakuma, Hiroshi
    Ichiki, Masahiro
    JOURNAL OF GEOPHYSICAL RESEARCH-SOLID EARTH, 2016, 121 (02) : 577 - 594
  • [28] Nb2O5-supported WO3:: a comparative study with WO3/Al2O3
    Martín, C
    Solana, G
    Malet, P
    Rives, V
    CATALYSIS TODAY, 2003, 78 (1-4) : 365 - 376
  • [29] A comparison of Kohler activation with nucleation for NaCl-H2O
    Mirabel, P
    Reiss, H
    Bowles, RK
    JOURNAL OF CHEMICAL PHYSICS, 2000, 113 (18): : 8194 - 8199
  • [30] Selective Synthesis of γ-WO3 and β-WO3⋅H2O by the Hydrothermal Treatment of Peroxotungstic Acid
    T. M. Bushkova
    A. A. Egorova
    A. V. Khoroshilov
    O. S. Ivanova
    A. D. Yapryntsev
    A. E. Baranchikov
    V. K. Ivanov
    Russian Journal of Inorganic Chemistry, 2021, 66 : 496 - 501
12345