Fabrication and Luminescence Properties of Ca2Gd8 (SiO4 )6O2:Er3+ Phosphors via Sol-Gel Process

Ca2RE8(SiO4)6O2(RE = Y, Gd, La) is a kind of ternary rare-earth-metal silicate with the oxyapatite structure, which was used as host materials for the luminescence of various rare earth and mercury-like ions. Ca2Gd8(SiO4)6O2: Er3 + phosphors were prepared through the sol-gel process. X-ray diffraction (XRD), scanning electron microscopy (SEM) and photoluminescence spectra were used to characterize the resulting phosphors. The results of XRD indicate that the phosphors crystallized completely at 1000℃. SEM study reveals that the average grain size is 400 ~ 1000 nm. In Ca2Gd8 (SiO4)6O2 : Er3+ phosphors, the Er3+ shows its characteristic green emission at 528 nm (2H11/2-4I15/2) and 548 nm (4 S3/2-4 I15/2) upon excitation into 382 nm, with an optimum doping concentration of 5% (mole fraction) of Gd3+ in the host lattices.