Preparation and Microstructure of Glass-ceramics and Ceramic Composite Materials

被引：0
|
作者：
(School of Materials Science and Engineering
机构：
来源：
Journal of Wuhan University of Technology(Materials Science Edition) | 2008年 / 04期
关键词：
CaO-Al2O3-SiO2; system; glass-ceramic; ceramic body;
D O I：
暂无
中图分类号：
TQ174.6 [生产过程与设备];
学科分类号：
080706 ;
摘要：
The technology and microstructure of glass-ceramics and ceramic composite materials were studied. A suitable ceramic body was chosen on the basis of the sintering temperature of CaO-Al2O3-SiO2 system glass-ceramics. According to the expansion coefficient of the ceramic body, that of CaO-Al2O3-SiO2 system glass-ceramics was adjusted. β-wollastonite was found present as the major crystalline phase in glass-ceramic. The CaO-Al2O3-SiO2 system glass-ceramic layer and ceramic body could be sintered together by adjusting the sintering period. The compositions of glass-ceramic layer and ceramic body diffuse mutually at 1 100 ℃, resulting in an interface between them. To achieve good sintered properties of glass-ceramics and the chosen ceramic body, at least a four-hour sintering time is used.
引用
收藏
页码：562 / 565
页数：4
相关论文
共 50 条
  • [31] STRENGTH AND MICROSTRUCTURE IN LITHIUM DISILICATE GLASS-CERAMICS
    BOROM, MP
    DOREMUS, RH
    TURKALO, AM
    AMERICAN CERAMIC SOCIETY BULLETIN, 1973, 52 (09): : 716 - 716
  • [32] Microstructure of Transparent Strontium Fresnoite Glass-Ceramics
    Wisniewski, Wolfgang
    Takano, Kazuya
    Takahashi, Yoshihiro
    Fujiwara, Takumi
    Ruessel, Christian
    SCIENTIFIC REPORTS, 2015, 5
  • [33] Microstructure of Transparent Strontium Fresnoite Glass-Ceramics
    Wolfgang Wisniewski
    Kazuya Takano
    Yoshihiro Takahashi
    Takumi Fujiwara
    Christian Rüssel
    Scientific Reports, 5
  • [34] EFFECT OF MICROSTRUCTURE ON RELIABILITY PREDICTIONS FOR GLASS-CERAMICS
    COOK, RF
    FREIMAN, SW
    BAKER, TL
    MATERIALS SCIENCE AND ENGINEERING, 1986, 77 (1-2): : 199 - 212
  • [35] Preparation of Glass-ceramics Using Waste Glass and Kaliophilite
    Si, Wei
    Chen, Sheng
    Ding, Chao
    Cailiao Daobao/Materials Reports, 2018, 32 : 110 - 113
  • [36] Synthesis of organoyttroxanealumoxanesiloxanes and preparation of glass and glass-ceramics on their base
    Shcherbakova, G. I.
    Storozhenko, P. A.
    Kutinova, N. B.
    Krivtsova, N. S.
    Varfolomeev, M. S.
    Movchan, T. L.
    Sidorov, D. V.
    Kuznetsova, M. G.
    Kuznetsova, T. M.
    Yurkov, G. Yu.
    Ashmarin, A. A.
    INORGANIC MATERIALS, 2014, 50 (03) : 306 - 313
  • [37] Synthesis of organoyttroxanealumoxanesiloxanes and preparation of glass and glass-ceramics on their base
    G. I. Shcherbakova
    P. A. Storozhenko
    N. B. Kutinova
    N. S. Krivtsova
    M. S. Varfolomeev
    T. L. Movchan
    D. V. Sidorov
    M. G. Kuznetsova
    T. M. Kuznetsova
    G. Yu. Yurkov
    A. A. Ashmarin
    Inorganic Materials, 2014, 50 : 306 - 313
  • [38] Fabrication of glass-ceramics composite by infiltration of lithium tetraborate glass into porous magnesium aluminate spinel ceramic
    Kulrat, Nattawat
    Busabok, Chumphol
    Intarasiri, Saweat
    Dangtip, Somsak
    Khongwong, Wasana
    JOURNAL OF METALS MATERIALS AND MINERALS, 2023, 33 (01): : 89 - 94
  • [39] Fabrication and Characterization of Modified Fluorescent Glass-Ceramics Composite from Waste Materials
    Nnaji, R. N.
    Agunsoye, J. O.
    Bodude, M. A.
    Fayomi, O. S. I.
    Talabi, I. O.
    MATERIALS FOCUS, 2018, 7 (04) : 529 - 534
  • [40] Preparation and properties of barium aluminosilicate glass-ceramics
    Wancheng Zhou
    Litong Zhang
    Jueming Yang
    Journal of Materials Science, 1997, 32 : 4833 - 4836
12345