INFLUENCE OF SURFACE HARDENING ON CONTACT FATIGUE LIFE OF NODULAR CAST IRON

被引：0
|
作者：
TAO Zengyi LUO Jiaming Huazhong University of Science and Technology
机构：
来源：
Acta Metallurgica Sinica(English Edition) | 1990年 / 03期
关键词：
surface hardening; contact fatigue life; laser melting; induction hardening;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The influence of laser surface melting and induction hardening on the surface structure,con-tact fatigue life and failure behaviour of the nodular cast iron has been investigated.The con-tact fatigue life can be improved by both laser treatment and induction hardening,but the fail-ure process and type are different from each other.The former is due to lumpy and deep spal-ling caused by crack propagation between the quenching zone and the substrate,and the latteris due to nubby and surface flaking caused by the oil wedged action into surface cracks.
引用
收藏
页码：188 / 193
页数：6
相关论文
共 50 条
  • [31] Influence of surface hardening by laser irradiation on the loss factor of cast iron
    Hiromasa Adachi
    Yoshihiko Masuo
    Teruo Hasegawa
    Journal of Materials Research, 1998, 13 : 1656 - 1659
  • [32] Influence of surface hardening by laser irradiation on the loss factor of cast iron
    Adachi, H
    Masuo, Y
    Hasegawa, T
    JOURNAL OF MATERIALS RESEARCH, 1998, 13 (06) : 1656 - 1659
  • [33] THE ENHANCEMENT OF THE FATIGUE HARDENING AND THE FATIGUE LIFE OF IRON
    GUIU, F
    DULNIAK, R
    SCHERNICKAU, NR
    EDWARDS, BC
    SCRIPTA METALLURGICA, 1981, 15 (07): : 727 - 732
  • [34] Fatigue Design of Ferritic-Pearlitic Nodular Cast Iron Components with Surface Discontinuities
    Groza, Marton
    Varadi, Karoly
    STROJNISKI VESTNIK-JOURNAL OF MECHANICAL ENGINEERING, 2018, 64 (06): : 373 - 382
  • [35] Influence of overloads on the fatigue crack growth in nodular cast iron: experiments and numerical simulation
    Mottitschka, T.
    Pusch, G.
    Biermann, H.
    Zybell, L.
    Kuna, M.
    FATIGUE 2010, 2010, 2 (01): : 1557 - 1567
  • [36] High cycle variable amplitude fatigue of a nodular cast iron
    Marquis, GB
    Rabb, BR
    Karjalainen-Roikonen, P
    FATIGUE TESTING AND ANALYSIS UNDER VARIABLE AMPLITUDE LOADING CONDITIONS, 2005, 1439 : 215 - 231
  • [37] A Novel Micromechanics Approach for Understanding of Fatigue in Nodular Cast Iron
    Lukhi, Mehul
    Huetter, Geralf
    Kuna, Meinhard
    ECF22 - LOADING AND ENVIRONMENTAL EFFECTS ON STRUCTURAL INTEGRITY, 2018, 13 : 607 - 612
  • [38] Experimental and Numerical Investigation of Fatigue Behaviour of Nodular Cast Iron
    Canzar, P.
    Tonkovic, Z.
    Bakic, A.
    Kodvanj, J.
    ADVANCES IN FRACTURE AND DAMAGE MECHANICS X, 2012, 488-489 : 182 - 185
  • [39] A new method for prediction of nodular cast iron fatigue limit
    Costa, N.
    Machado, N.
    Silva, F. S.
    INTERNATIONAL JOURNAL OF FATIGUE, 2010, 32 (07) : 988 - 995
  • [40] Fatigue limit of nodular cast iron containing casting defects
    Nadot, Y
    Mendez, J
    Ranganathan, N
    Béranger, AS
    ECF 12: FRACTURE FROM DEFECTS, VOLS. I-III, 1998, : 85 - 90
12345