Multilayer Clad Plate of Stainless Steel/Aluminum/ Aluminum Alloy

被引：0

作者：

袁家伟 ^{[1
]}

庞玉华 ^{[1
]}

机构：

[1] School of Metallurgy Engineering, Xi’an University of Architecture & Technology

来源：

Journal of Wuhan University of Technology(Materials Science) | 2011年 / 01期

关键词：

multilayer clad plate; hot rolling; bonding strength; stretch strength;

D O I：

暂无

中图分类号：

TG146.21 [];

学科分类号：

080502 ;

摘要：

The 3, 5, 20 layer clad plate from austenitic stainless steel, pure aluminum and aluminum alloy sheets were fabricated in different ways. The stretch and interface properties were measured. The result shows that 20 layer clad plate is better than the others. Well-bonded clad plate was successfully obtained in the following procedure: Basic clad sheet from 18 layer Al1060/Al3003 sheets was firstly obtained with an initial rolling reduction of 44% at 450 ℃, followed by annealing at 300 ℃, and then with reduction of 50% at 550 ℃ from STS304 on each side. The best 20 layer clad plate was of 129 MPa bonding strength and 225 MPa stretch strength.

引用

页码：111 / 113

页数：3

共 50 条

[31] Development of stainless steel clad alloy steel bars
Thavornun, S
Mishra, B
Moore, JJ
Olson, DL
PROCESSING AND FABRICATION OF ADVANCED MATERIALS IV, 1996, : 79 - 96
[32] Resistance Rivet Welding of Aluminum Alloy and Steel with a Supplementary Plate
Shi, Hongxin
Zhu, Shibo
Hu, Yanling
Guo, Han
Xiao, Xiao
Qiu, Ranfeng
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2024, 33 (23) : 13213 - 13220
[33] Deformation characteristics of aluminum-clad stainless steel sheet under uniaxial tension
Mori, T
Kurimoto, S
JOURNAL OF MANUFACTURING SCIENCE AND ENGINEERING-TRANSACTIONS OF THE ASME, 1998, 120 (01): : 179 - 184
[34] Influence of punch profile radius on deep drawability of stainless steel and aluminum clad sheet
Nippon Kikai Gakkai Ronbunshu C Hen, 594 (767-772):
[35] JOINING STAINLESS STEEL TO ALUMINUM
ALEXANDE.RJ
WILLIAMS, CO
WELDING JOURNAL, 1970, 49 (12) : 925 - &
[36] A MULTILAYER CLAD ALUMINUM MATERIAL WITH IMPROVED BRAZING PROPERTIES
ENGSTROM, H
GULLMAN, LO
WELDING JOURNAL, 1988, 67 (10) : S222 - S226
[37] Multilayer clad aluminum material with improved brazing properties
Engstroem, H.
Gullman, L.O.
Welding Journal (Miami, Fla), 1988, 67 (10):
[38] Roll Casting of Aluminum Alloy Clad Strip
Nakamura, R.
Haga, T.
Tsuge, H.
Watari, H.
Kumai, S.
INTERNATIONAL CONFERENCE ON ADVANCES IN MATERIALS AND PROCESSING TECHNOLOGIES, PTS ONE AND TWO, 2010, 1315 : 650 - +
[39] Effect of surface treatment on bonding strength of hot rolled steel aluminum clad plate
Deng, Z. J.
Yu, C.
Xiao, H.
19TH INTERNATIONAL CONFERENCE ON METAL FORMING, MF 2022, 2022, 1270
[40] Fatigue Propagation in a Clad Aluminum Alloy.
Spinelli, Isa Maria Muller
Spinelli, Dirceu
Metalurgia ABM, 1982, 38 (300): : 653 - 657

← 1 2 3 4 5 →