Influence of Nucleation Agents Concentration on Crystallization Structure and Properties of Glass-ceramics

Deep color glass-ceramics is prepared by using gold tailings as the main raw material, and Cr2O3 is added as nucleation agent. Influence of different Cr2O3 additions on crystallization structure and properties of CaO-MgO-Al2O3-SiO2 glass-ceramics has been discussed so as to select optimum additions. DTA is employed to determine optimum crystallization and nucleation temperatures; XRD and SEM are used to characterize microstructure of each sample; and performance indexes, such as water absorption, bulk density, flexural strength and so on, are also determined. Experimental results show that when 3wt% Cr2O3 is introduced, fine glass-ceramics with diopside as the main crystal and Ca-Fe diopside as the second-crystal is obtained, and its corresponding performance indexes are as follows: water absorption 0.12%, bulk density 2.56 g/cm3, and flexural strength 70.01 Mpa.