Carbide precipitation behavior and mechanical properties of micro-alloyed medium Mn steel

被引:4
|
作者
Luhan Hao [1 ]
Xiang Ji [1 ,2 ]
Guangqian Zhang [1 ]
Wei Zhao [1 ]
Mingyue Sun [2 ]
Yan Peng [1 ]
机构
[1] National Engineering Research Center for Equipment and Technology of Cold Strip Rolling, Yanshan University
[2] Shenyang National Laboratory for Material Science, Institute of Metal Research, Chinese Academy of Sciences
基金
中国国家自然科学基金;
关键词
Advanced high strength steel; Medium Mn steel; Thermal deformation; Intercritical annealing; The product of strength and elongation;
D O I
暂无
中图分类号
TG142.1 [钢的组织与性能];
学科分类号
摘要
The carbide precipitation behavior and mechanical properties of advanced high strength steel deformed at different temperatures are investigated by X-ray diffractometer(XRD),scanning electron microscope(SEM),transmission electron microscope(TEM) equipped with an energy dispersing spectroscopy(EDS),and tensile tests.The medium Mn steel was subjected to controlled deformation up to 70% at 750℃,850℃,950℃,and 1050℃,and then quenched with water to room temperature,followed by intercritical annealing at 630℃ for 10 min.In comparison with the undeformed and quenched specimen,it can be concluded that acicular cementite precipitates during the quenching and cooling process,while granular NbC is the deformation induced precipitate and grows during the following annealing process.As the deformation temperature increases from 750℃ to 1050℃,the product of strength and elongation increases at first and then decreases.The smallest average size of second phase particles(20 nm) and the best mechanical properties(32.5 GPa%) can be obtained at the deformation temperature of 950℃.
引用
收藏
页码:122 / 130
页数:9
相关论文
共 50 条
  • [41] THERMOMECHANICAL PROCESSING OF MICRO-ALLOYED STEEL
    Podany, Pavel
    Martinek, Petr
    MATERIALI IN TEHNOLOGIJE, 2014, 48 (06): : 855 - 859
  • [42] Machine learning interphase precipitation behavior of Ti micro-alloyed steel guided by physical metallurgy principle
    Li, Xin
    Jiang, Qiming
    Zhou, Xiaoguang
    Wu, Siwei
    Cao, Guangming
    Liu, Zhenyu
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2023, 25 : 2641 - 2653
  • [43] Effect of quenching and partitioning time on microstructure and mechanical properties of low carbon micro-alloyed steel
    Arif, Sk Md
    Ghorai, Satadal
    Bar, Himadri Nandan
    Mandal, Durbadal
    MATERIALS TODAY-PROCEEDINGS, 2022, 66 : 3865 - 3869
  • [44] Microstructure-Tensile Properties Relationship and Austenite Stability of a Nb-Mo Micro-Alloyed Medium-Mn TRIP Steel
    Liu, Chunquan
    Peng, Qichun
    Xue, Zhengliang
    Deng, Mingming
    Wang, Shijie
    Yang, Chengwei
    METALS, 2018, 8 (08):
  • [45] Static recrystallization behavior of hot deformed austenite for micro-alloyed steel
    Huang, Jie
    Xu, Zhou
    Xing, Xin
    Journal of Materials Science and Technology, 2003, 19 (SUPPL.): : 117 - 118
  • [46] Hot deformation behavior of Cr micro-alloyed low carbon steel
    Dong, Hai-Feng
    Cai, Da-Yong
    Wang, Yu-Hui
    Yang, Qing-Xiang
    Liao, Bo
    Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment, 2009, 30 (06): : 47 - 50
  • [47] Effect of Nitrogen on Microstructure and Mechanical Properties for Simulated CGHAZ of Normalized Vanadium Micro-alloyed Steel
    Chai F.
    Shi Z.
    Yang C.
    Wang J.
    Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research, 2019, 33 (11): : 848 - 856
  • [48] Static recrystallization behavior of hot deformed austenite for micro-alloyed steel
    Huang, J
    Xu, Z
    Xing, X
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2003, 19 : 117 - 118
  • [49] Mechanical behaviour of low carbon steel micro-alloyed with Nb, V, and Ti
    Darsouni, Abdelrrazek.
    Boudebane, Azzedine
    ANNALES DE CHIMIE-SCIENCE DES MATERIAUX, 2011, 36 (02): : 87 - 98
  • [50] Strain-induced Precipitation in Ti Micro-alloyed Interstitial-free Steel
    Hui, Ya-jun
    Yu, Yang
    Wang, Lin
    Wang, Chang
    Li, Wen-yuan
    Chen, Bin
    JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2016, 23 (04) : 385 - 392