The grain refining mechanism of C-Mn steel by CSP

被引：0
|
作者：
SONG Chang
机构：
来源：
BaosteelTechnicalResearch | 2010年 / 4(S1)卷 / S1期
关键词：
CSP; grain refinement; repeated phase transformation;
D O I：
暂无
中图分类号：
TG335 [轧制工艺];
学科分类号：
摘要：
The grain refining mechanism of C-Mn steel sheet on compact strip production(CSP) line was investigated in this study.The grain was about 100μm after F1 pass and decreased all the way of the rolling process(F2-F6) to 15μm.Repeated phase transformation experiment was conducted to the steel for grain refinement.The phase transformation at 860℃and 920℃can refine the grain size to 7.5μm.
引用
收藏
页码：29 / 29
页数：1
相关论文
共 50 条
  • [41] THE EFFECT OF NITROGEN AND STRAIN AGING OF C-MN STEEL WELDS
    MANDZIEJ, ST
    SCRIPTA METALLURGICA ET MATERIALIA, 1992, 27 (07): : 793 - 798
  • [42] Microstructural effect on tensile and fatigue behaviour of C-Mn steel
    Hussain, K
    DelosRios, RR
    JOURNAL OF MATERIALS SCIENCE, 1997, 32 (13) : 3565 - 3569
  • [43] Probabilistic modelling of the size effect on ductility of a C-Mn steel
    Carassou, S
    Soilleux, M
    Marini, B
    JOURNAL DE PHYSIQUE IV, 1998, 8 (P8): : 63 - 70
  • [44] Effect of Nb on grain growth of ferrite in C-Mn steel during isothermal holding after severe deformation
    Hong, SC
    Lim, SH
    Hong, HS
    Lee, KJ
    Shin, DH
    Lee, KS
    MATERIALS SCIENCE AND TECHNOLOGY, 2004, 20 (02) : 207 - 212
  • [45] Effect of ultrafine grain structure on strain hardening of C-Mn steel warm rolled and subjected to intercritical annealing
    Department of Metallurgical and Materials Engineering, Federal University of Minas Gerais, MG, Brazil
    Mater. Sci. Technol., 12 (1470-1476):
  • [46] Strain driven grain boundary sliding and/or rotation during tensile deformation of ultrafine grained C-Mn steel
    Du, L. X.
    Yao, S. J.
    Zhou, M.
    Wang, G. D.
    MATERIALS SCIENCE AND TECHNOLOGY, 2011, 27 (12) : 1814 - 1818
  • [47] Further study on the mechanism of the ductile-to-brittle fracture transition in C-Mn base and weld steel
    Wang, GZ
    Chen, JH
    Li, ZH
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1997, 28 (08): : 1689 - 1698
  • [48] Further study on the mechanism of the ductile-to-brittle fracture transition in C-Mn base and weld steel
    G. Z. Wang
    J. H. Chen
    Z. H. Li
    Metallurgical and Materials Transactions A, 1997, 28 : 1689 - 1698
  • [49] CSP线生产C-Mn系热轧双相钢的工业试验
    刘彦春
    董瑞峰
    屈文胜
    闫波
    王建钢
    王国栋
    轧钢, 2006, (04) : 1 - 4
  • [50] CSP生产C-Mn钢薄带组织与表面裂纹研究
    张超
    宋畅
    韩斌
    谭佳梅
    郭茜
    吴润
    钢铁研究学报, 2011, (05) : 50 - 54
12345