Deposition of electroless Ni-P/Ni-W-P duplex coatings on AZ91D magnesium alloy

被引：3
|
作者：
陈晓明 [1 ]
李光玉 [1 ]
连建设 [1 ]
机构：
[1] Key Laboratory of Automobile Materials,Ministry of Education,College of Materials Science and Engineering,Jilin University
来源：
Transactions of Nonferrous Metals Society of China | 2008年 / 18(S1)卷 / S1期
关键词：
corrosion resistance; electroless deposition; Ni-W-P alloy; acid-sulfate nickel;
D O I：
暂无
中图分类号：
TG146.22 [];
学科分类号：
摘要：
The electroless Ni-P/Ni-W-P duplex coatings were deposited directly on AZ91D magnesium alloy by an acid-sulfate nickel bath.Nickel sulphate and sodium tungstate were used as metal ion sources and sodium hypophosphite was used as reducing agent.The coating was characterized for its structure,morphologies,microhardness and corrosion properties.The presence of dense and coarse nodules in the duplex coatings was observed by SEM and EDS.Tungsten content in Ni-P/Ni-W-P alloy is about 0.65%(mass fraction) and the phosphorus content is 8.18%(mass fraction).The microhardness of the coatings is 622 VHN.The coating shows good adhesion to the substrate.The results of electrochemical analysis,the porosity and the immersion test show that Ni-P/Ni-W-P duplex coatings possess noble anticorrosion properties to protect the AZ91D magnesium alloy.
引用
收藏
页码：323 / 328
页数：6
相关论文
共 50 条
  • [21] Electroless Ni-P plating on AZ91D magnesium alloy from a sulfate solution
    Gu, CD
    Lian, JS
    Li, GY
    Niu, LY
    Jiang, ZH
    JOURNAL OF ALLOYS AND COMPOUNDS, 2005, 391 (1-2) : 104 - 109
  • [22] Deposition Mechanism of Eletroless Plating of Ni-P on AZ91D Magnesium Alloy
    Qian Jiangang
    Teng Xiaoming
    Liu Yufen
    Huang Wei
    RARE METAL MATERIALS AND ENGINEERING, 2010, 39 (09) : 1593 - 1597
  • [23] Friction and wear behavior of electroless Ni-P and Ni-W-P alloy coatings
    Palaniappa, M.
    Seshadri, S. K.
    WEAR, 2008, 265 (5-6) : 735 - 740
  • [24] Optimizing parameters affecting electroless Ni-P coatings on AZ91D magnesium alloy as corrosion protection barriers
    Fakiha El-Taib Heakal
    Madiha A. Shoeib
    Maanoum A. Maanoum
    Protection of Metals and Physical Chemistry of Surfaces, 2017, 53 : 177 - 187
  • [25] Optimizing Parameters Affecting Electroless Ni-P Coatings on AZ91D Magnesium Alloy as Corrosion Protection Barriers
    Heakal, Fakiha El-Taib
    Shoeib, Madiha A.
    Maanoum, A. Maanoum
    PROTECTION OF METALS AND PHYSICAL CHEMISTRY OF SURFACES, 2017, 53 (01) : 177 - 187
  • [26] Preparation and corrosion resistance of electroless Ni-P/SiC functionally gradient coatings on AZ91D magnesium alloy
    Wang, Hui-Long
    Liu, Ling-Yun
    Dou, Yong
    Zhang, Wen-Zhu
    Jiang, Wen-Feng
    APPLIED SURFACE SCIENCE, 2013, 286 : 319 - 327
  • [27] Comparative study on corrosion protection properties of electroless Ni-P-ZrO2 and Ni-P coatings on AZ91D magnesium alloy
    Song, Y. W.
    Shan, D. Y.
    Han, E. H.
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2007, 58 (07): : 506 - 510
  • [28] Electroless Ni-P Deposition on AZ91 D Magnesium Alloy Prepared by Molybdate Chemical Conversion Coatings
    Elsentriecy, Hassan H.
    Azumi, Kazuhisa
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2009, 156 (02) : D70 - D77
  • [29] Electroless Ni-P layer with a chromium-free pretreatment on AZ91D magnesium alloy
    Zhang, W. X.
    He, J. G.
    Jiang, Z. H.
    Jiang, Q.
    Lian, J. S.
    SURFACE & COATINGS TECHNOLOGY, 2007, 201 (08): : 4594 - 4600
  • [30] Corrosion and wear properties of electroless Ni-P plating layer on AZ91D magnesium alloy
    Li Zhong-hou
    Chen Zhi-yong
    Liu Sha-sha
    Zheng Feng
    Dai A-gan
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2008, 18 (04) : 819 - 824
12345