Oxidation behavior of pure W and W-0.5 wt% ZrC at 700 °C and 900 °C

被引：0

作者：

Wang, Yongkui ^{[1
]}

Huang, Xiaochen ^{[1
]}

Lv, Changpeng ^{[1
]}

Wu, Zhong ^{[1
]}

Ge, Jinlong ^{[1
]}

Ma, Jianguo ^{[2
]}

Zhang, Xueqi ^{[3
]}

机构：

[1] Bengbu Univ, Sch Mat & Chem Engn, Bengbu 233030, Peoples R China

[2] Chinese Acad Sci, Inst Plasma Phys, Hefei 230000, Peoples R China

[3] Hefei ADChem Semitech co Ltd, Hefei 230001, Peoples R China

来源：

NUCLEAR MATERIALS AND ENERGY | 2025年 / 43卷

关键词：

Pure tungsten; WZC05; Oxide layer; Oxidation resistance; Oxidation behavior; ALLOYS; MICROSTRUCTURE;

D O I：

10.1016/j.nme.2025.101922

中图分类号：

TL [原子能技术]; O571 [原子核物理学];

学科分类号：

0827 ; 082701 ;

摘要：

This study investigates the oxidative behavior of pure tungsten and a W-0.5 wt% ZrC alloy (WZC05), was examined. Both materials were fabricated via sintering and hot rolling. The alloys were exposed to air at 700 degrees C for 20 h and to air at 900 degrees C for 8 h to analyze surface morphology, oxidation resistance, and oxidation behavior of pure tungsten and WZC05. WZC05 exhibited a significantly smaller grain size than pure tungsten. At 700 degrees C, the "positive effect of grain size," caused a higher oxidation rate in pure tungsten compared with that in WZC05. After air oxidation for 20 h at 700 degrees C, the thickness of the oxide layer on pure tungsten reached 320 mu m, whereas that on WZC05 was only 202 mu m. At 900 degrees C, the dense oxide layer was destroyed owing to the formation of volatile WO3, resulting in similar oxidation rates for pure tungsten and WZC05. Scanning electron micrographs revealed that the oxidized tungsten materials had a layered structure.

引用

页数：7

共 50 条

[31] The fabrication of dense, W-rich, W/ZRC composites by the prima-DCP process at 1300°C
Dickerson, MB
Snyder, RL
Sandhage, KH
PROCESSING AND FABRICATION OF ADVANCED MATERIALS XI, 2003, : 403 - 412
[32] Microstructures, Mechanical Properties and Thermal Conductivities of W-0.5 wt.% TiC Alloys Prepared via Ball Milling and Wet Chemical Method
Lang, Shaoting
Yan, Qingzhi
Sun, Ningbo
Zhang, Xiaoxin
Ge, Changchun
JOM, 2017, 69 (10) : 1992 - 1996
[33] Microstructures, Mechanical Properties and Thermal Conductivities of W-0.5 wt.%TiC Alloys Prepared via Ball Milling and Wet Chemical Method
Shaoting Lang
Qingzhi Yan
Ningbo Sun
Xiaoxin Zhang
Changchun Ge
JOM, 2017, 69 : 1992 - 1996
[34] Phase equilibria in the Ni-Al-W system at 900°C
Broz, P
Bursík, J
Stará, Z
MONATSHEFTE FUR CHEMIE, 2005, 136 (11): : 1915 - 1920
[35] THE OXIDATION BEHAVIOR OF TANTALUM AT 700-DEGREES-C-1000-DEGREES-C
KOFSTAD, P
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1963, 110 (06) : 491 - 501
[36] The oxidation behavior of a ductile Hf0.5Nb0.5Ta0.5Ti1.5Zr refractory high-entropy alloy in pure oxygen condition at 500-900 °C
Wang, Y. Z.
Gao, N.
Liu, X. W.
Chen, W. M.
Zheng, H. T.
JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2023, 25 : 5457 - 5468
[37] CORROSION OF MANGANESE IN PURE SO2 BETWEEN 700-DEGREES-C AND 900-DEGREES-C
DEASMUNDIS, C
BOTTINO, C
CHIMICA & L INDUSTRIA, 1979, 61 (05): : 451 - 451
[38] Oxidation behavior of ZrB2-SiC-ZrC at 1700 °C
Kubota, Yuki
Tanaka, Hiroki
Arai, Yutaro
Inoue, Ryo
Kogo, Yasuo
Goto, Ken
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2017, 37 (04) : 1187 - 1194
[39] OXIDATION OF U-14 AT PERCENT ZR BETWEEN 700 AND 900 DEGREES C
CATHCART, JV
PETERSEN, GF
OXIDATION OF METALS, 1973, 7 (01): : 31 - 43
[40] Oxidation behavior of Cu-20Ni-30Cr alloy in pure O2 at 700°C and 800°C
Zhang, XJ
Niu, Y
Wu, WT
RARE METAL MATERIALS AND ENGINEERING, 2005, 34 (08) : 1271 - 1274

← 1 2 3 4 5 →