Interface kinetic manipulation enabling efficient and reliable Mg3Sb2 thermoelectrics

Development of efficient and reliable thermoelectric generators is vital for the sustainable utilization of energy, yet interfacial losses and failures between the thermoelectric materials and the electrodes pose a significant obstacle. Existing approaches typically rely on thermodynamic equilibrium to obtain effective interfacial barrier layers, which underestimates the critical factors of interfacial reaction and diffusion kinetics. Here, we develop a desirable barrier layer by leveraging the distinct chemical reaction activities and diffusion behaviors during sintering and operation. Titanium foil is identified as a suitable barrier layer for Mg3Sb2-based thermoelectric materials due to the creation of a highly reactive ternary MgTiSb metastable phase during sintering, which then transforms to stable binary Ti-Sb alloys during operation. Additionally, titanium foil is advantageous due to its dense structure, affordability, and ease of manufacturing. The interfacial contact resistivity reaches below 5 mu Omega<middle dot>cm2, resulting in a Mg3Sb2-based module efficiency of up to 11% at a temperature difference of 440 K, which exceeds that of most state-of-the-art medium-temperature thermoelectric modules. Furthermore, the robust Ti foil/Mg3(Sb,Bi)2 joints endow Mg3Sb2-based single-legs as well as modules with negligible degradation over long-term thermal cycles, thereby paving the way for efficient and sustainable waste heat recovery applications. The authors identify an ideal thermoelectric barrier layer by exploiting distinct chemical reaction activities and diffusion behaviors during sintering and operation, achieving 11% module efficiency at 723 K with enhanced long-term stability.