Effects of pitting corrosion on the void growth of thin steel plates

被引：0

作者：

Zhang, Haijiang ^{[1
,2
]}

Liu, Hongbo ^{[1
]}

Xu, Shanhua ^{[2
]}

Zhao, Yajun ^{[1
]}

Zhang, Zongxing ^{[2
]}

Meng, Qingxuan ^{[1
]}

机构：

[1] Hebei Univ Engn, Sch Civil Engn, Handan 056038, Peoples R China

[2] Xian Univ Architecture & Technol, Sch Civil Engn, Xian 710055, Peoples R China

来源：

ENGINEERING FRACTURE MECHANICS | 2025年 / 315卷

基金：

中国国家自然科学基金;

关键词：

Corrosion; Voids growth; Corroded thin steel plates; Ductile fracture; Microscopic mechanism; DUCTILE FRACTURE; LODE PARAMETER; STRESS TRIAXIALITY; NUCLEATION; STRENGTH; CRITERION; FAILURE;

D O I：

10.1016/j.engfracmech.2024.110796

中图分类号：

O3 [力学];

学科分类号：

08 ; 0801 ;

摘要：

Corrosion will lead to the serious degradation of the ductile fracture property of thin-walled steel structures because of its small wall thickness. To determine the effects of corrosion pit on the ductile fracture behaviors of thin steel plates, it is necessary to study the ductile fracture microscopic mechanism of corroded thin steel plates. This paper investigated the ductile fracture microscopic mechanism of corroded thin steel plates based on the numerical cubic cell models. A series of computational cubic cell models considering pit depth and shape effects were established. The effects of surface pits depth and shape on microscopic void deformation mechanism in the fracture point of thin steel plates were studied. The ductile fracture criterion of corroded thin steel plates was established according to the micro-voids deformation mechanism, and the average relative error of the nominal fracture strain epsilon n,f calculated by the proposed ductile fracture criterion was 13.62%.

引用

页数：18

共 50 条

[41] Inhibition of Pitting Corrosion of the Stainless Steel by Dipyridinium Salts
Obaid, A. Y.
Al-Thabaiti, S. A.
Qusti, A. H.
Hermas, A. A.
ASIAN JOURNAL OF CHEMISTRY, 2013, 25 (07) : 3781 - 3788
[42] Inhibition of Pitting Corrosion on Type 304 Stainless Steel
Lian, Zhouyang
MATERIALS PERFORMANCE, 2017, 56 (12) : 54 - 56
[43] Effect of simulated pitting corrosion on the tensile properties of steel
Sheng, Jie
Xia, Junwu
CONSTRUCTION AND BUILDING MATERIALS, 2017, 131 : 90 - 100
[44] Peridynamic Modeling of Repassivation in Pitting Corrosion of Stainless Steel
Jafarzadeh, Siavash
Chen, Ziguang
Bobaru, Florin
CORROSION, 2018, 74 (04) : 393 - 414
[45] Extreme Value Statistics for Pitting Corrosion of Steel Pipelines
Melchers, R. E.
Ahammed, M.
PROCEEDINGS OF THE 25TH AUSTRALASIAN CONFERENCE ON MECHANICS OF STRUCTURES AND MATERIALS (ACMSM25), 2020, 37 : 667 - 676
[46] On the Characteristic Potentials of Pitting Corrosion of Compact and Powder Steel
I. I. Zamaletdinov
I. N. Baryshnikov
Protection of Metals and Physical Chemistry of Surfaces, 2017, 53 : 1227 - 1234
[47] CORROSION OF RUST PROOF STEEL BY PITTING OF CONDENSATOR TUBES
LONG
METALLURGIA ITALIANA, 1968, 60 (12): : 321 - &
[48] INITIATION EVENTS FOR PITTING CORROSION OF STAINLESS-STEEL
RILEY, AM
WELLS, DB
WILLIAMS, DE
CORROSION SCIENCE, 1991, 32 (12) : 1307 - 1313
[49] PITTING CORROSION OF SENSITIZED FERRITIC STAINLESS-STEEL
RAREY, CR
ARONSON, AH
CORROSION, 1972, 28 (07) : 255 - &
[50] TEMPERATURE-DEPENDENCE OF PITTING CORROSION IN CHROMIUM STEEL
TOUSEK, J
KOVOVE MATERIALY-METALLIC MATERIALS, 1978, 16 (04): : 476 - 485

← 1 2 3 4 5 →