Optimization of bobbin tool friction stir welding parameters of AZ31 magnesium alloy based on FEM and its influence mechanism on mechanical properties

Based on the 3D transient heat transfer theory, the finite element model of bobbin tool friction stir welding (BT-FSW) of AZ31 magnesium alloy sheet is established. The effects of different process parameters on the quality of BT-FSW joint of magnesium alloy were discussed using temperature distribution, mechanical properties, fracture morphology analysis, and EDS element distribution analysis. The results show that in the process of BT-FSW, the cross-section temperature of the plate is symmetrically distributed in an hourglass shape, the AS is slightly lower than that of RS, and the transverse temperature is distributed in an 'M' shape. When the rotating speed is 700 rpm and the welding speed is 180 mm/min, the weld surface is smooth, and its ultimate tensile strength can reach 81.82% of the base metal strength. The tensile specimen is quasi-cleavage fracture. When the heat input is insufficient, there are a lot of Al8Mn5 Precipitated phases in the TMAZ fracture zone, which increases the fracture brittleness of the joint. When the heat input is enough, the precipitated phase dissolves evenly, the river-like fracture surface of the joint retains the dimple characteristics, and the mechanical properties are improved.