Adsorption technique using new semi-IPN hydrogels for high removal of methylene blue dye from aqueous solutions

Six new semi-IPN hydrogels using 2-acrylamido-methylpropane-1-sulfonic acid (AMPS) and Gelatin at different ratios through redox polymerization were prepared. Methylene-bisacrylamide and glutaraldehyde were used as the crosslinking agents for AMPS and Gelatin, respectively. The hydrogels' swelling ratios and surface morphologies were analyzed using SEM for characterization. Porosity and specific surface area using the Brunauer-Emmett-Teller technique. DSC and Tg were also used for the thermal analysis of the prepared hydrogels, which show trans-glass temperature (Tg) higher than their raw materials AMPS and Gelatin. The prepared hydrogels were used to eliminate the cationic dye MB from the water-based solutions with an initial concentration of 600 ppm. The study discovered that the N9 and N10 hydrogels were extremely effective at removing a certain dye from aqueous solutions with an optimum pH level of 11 and an optimum temperature of 65 degrees C. Both N9 and N10 achieved high removal efficiencies, reaching equilibrium at 90 min, whereas the other hydrogels required 120 min. N9 performed slightly better at 1078.919 mg/g and N10 at 1057.404 mg/g. The adsorption behavior of the two hydrogels followed the Langmuir model. The hydrogels exhibited pseudo-second-order kinetics. The thermodynamic study cleared that the adsorption of MB dye was endothermic and spontaneous. Results also showed that the adsorption of dyes with hydrogels N9 and N10 is chemisorption in nature. Desorption studies were conducted using 0.1 M HCl and NaOH. HCl was found to be the best eluent for dye recovery.