Stress-relief cracking susceptibility of a new ferritic steel - Part 1: Single-pass heat-affected zone simulations

被引：0

作者：

Nawrocki, J.G. ^{[1
]}

Dupont, J.N. ^{[1
]}

Robino, C.V. ^{[2
]}

Marder, A.R. ^{[1
]}

机构：

[1] Dept. of Mat. Sci. and Engineering, Lehigh University, Bethlehem, PA, United States

[2] Materials Joining Dept., Sandia National Laboratories, Albuquerque, NM, United States

来源：

Welding Journal (Miami, Fla) | 2000年 / 79卷 / 12期

关键词：

Crack initiation - Durability - Grain boundaries - Heat affected zone - Metallographic microstructure - Scanning electron microscopy - Stress analysis;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Heat affected zone (HAZ) simulation techniques were used to investigate the stress relief cracking (SRC) response of conventional steels. Postweld heat treatment (PWHT) and thermal simulations were used for the purpose. Optical and scanning electron microscopy (SEM) using thermal cycles were used to study microstructure of the coarse-grained heat-affected zone (CGHAZ).

引用

共 50 条

[21] Case Study: Pitting and Stress Corrosion Cracking in Heat-Affected Zone of Welded Underground 304 Stainless Steel Pipe
Tawancy, H. M.
Al-Hadhrami, Luai M.
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2012, 21 (08) : 1757 - 1762
[22] Case Study: Pitting and Stress Corrosion Cracking in Heat-Affected Zone of Welded Underground 304 Stainless Steel Pipe
H. M. Tawancy
Luai. M. Al-Hadhrami
Journal of Materials Engineering and Performance, 2012, 21 : 1757 - 1762
[23] Stress corrosion cracking in the heat-affected zone of A508 steel welds under high-temperature water
Chung, Wei-Chih
Huang, Jiunn-Yuan
Tsay, Leu-Wen
Chen, Chun
JOURNAL OF NUCLEAR MATERIALS, 2011, 408 (01) : 125 - 128
[24] Reheat Cracking Susceptibility in Coarse Grained Heat-affected Zone of SA508-4 Steel for Nuclear Pressure Vessel
Chen Z.
Ma Y.
Xing S.
Bai Q.
Liu Y.
Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research, 2019, 33 (01): : 72 - 80
[25] Stress Corrosion Cracking of Simulated Weld Heat-Affected Zone on X100 Pipeline Steel in Carbonate/Bicarbonate Solution
Song Longfei
Liu Zhiyong
Li Xiaogang
Du Cuiwei
Journal of Materials Engineering and Performance, 2020, 29 : 2574 - 2585
[26] Stress corrosion cracking behavior of 16Mn steel and heat-affected zone in alkaline sulfide with different Ph value
Hao, Wen-Kui
Liu, Zhi-Yong
Ma, Yan
Du, Cui-Wei
Li, Xiao-Gang
Hu, Shan-Shan
Cailiao Gongcheng/Journal of Materials Engineering, 2015, 43 (03): : 28 - 34
[27] Stress Corrosion Cracking of Simulated Weld Heat-Affected Zone on X100 Pipeline Steel in Carbonate/Bicarbonate Solution
Song Longfei
Liu Zhiyong
Li Xiaogang
Du Cuiwei
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2020, 29 (04) : 2574 - 2585
[28] Effects of Nb on Stress Corrosion Cracking of Various Heat-Affected Zone Microstructures of E690 Steel under Cathodic Potential
Endian Fan
Qiyue Zhao
Heng Chen
Yanan Ma
Chao Hai
Ying Yang
Yunhua Huang
Xiaogang Li
Journal of Materials Engineering and Performance, 2023, 32 : 9926 - 9945
[29] INFLUENCE OF SOFTENED HEAT-AFFECTED ZONE ON STRESS ORIENTED HYDROGEN-INDUCED CRACKING OF A HIGH-STRENGTH LINE PIPE STEEL
TAKAHASHI, A
OGAWA, H
ISIJ INTERNATIONAL, 1995, 35 (10) : 1190 - 1195
[30] Effects of Nb on Stress Corrosion Cracking of Various Heat-Affected Zone Microstructures of E690 Steel under Cathodic Potential
Fan, Endian
Zhao, Qiyue
Chen, Heng
Ma, Yanan
Hai, Chao
Yang, Ying
Huang, Yunhua
Li, Xiaogang
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2023, 32 (21) : 9926 - 9945

← 1 2 3 4 5 →