Corrosion Behavior of the Al-Li-Cu-Mg Alloy.

被引：0
|
作者：
Braun, R.
Buhl, H.
机构：
来源：
Zeitschrift fuer Werkstofftechnik/Materials Technology and Testing | 1987年 / 18卷 / 08期
关键词：
AIRCRAFT MATERIALS - Light Metals - METALS TESTING - Corrosion - SURFACES - Microscopic Examination;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The localized corrosion behavior of the Al-Li-Cu-Mg alloy 8090-T651 (25 mm thick plate) was investigated using salt spray tests, the EXCO test and tests according to the MIL-H-6088F specification. These accelerated laboratory tests indicate that the material is susceptible to intergranular and exfoliation corrosion. The stress corrosion cracking behavior was studied under constant load, constant deformation and slow strain rate conditions. The material was found to be resistant to stress corrosion cracking in the long transverse direction. In the short transverse direction a threshold stress below 50 MPa was determined. The same values were measured for the conventional alloys 2014-T351 and 2024-T351. The fracture surfaces of specimens which failed due to stress corrosion cracking were examined using a scanning electron microscope. Fractographic features attributed to corrosion are discussed.
引用
收藏
页码：258 / 265
相关论文
共 50 条
  • [21] CRYSTALLINE AND QUASI-CRYSTALLINE STRUCTURES IN AN AL-LI-CU-MG ALLOY
    LOISEAU, A
    LAPASSET, G
    JOURNAL DE PHYSIQUE, 1986, 47 (C-3): : 331 - 340
  • [22] Rolling Effect on Serrated Flow in an Al-Li-Cu-Mg Alloy Plate
    Doglione, R.
    Ashtiani, P. Haghi
    Berdin, C.
    MATERIALS PERFORMANCE AND CHARACTERIZATION, 2015, 4 (01) : 73 - 86
  • [23] Evolution of texture and microstructure in a thermomechanically processed Al-Li-Cu-Mg alloy
    A. K. Singh
    G. G. Saha
    A. A. Gokhale
    R. K. Ray
    Metallurgical and Materials Transactions A, 1998, 29 : 665 - 675
  • [24] EFFECTS OF ENVIRONMENT AND MICROSTRUCTURE ON STRESS-CORROSION CRACK-PROPAGATION IN AN AL-LI-CU-MG ALLOY
    AHMAD, M
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1990, 125 (01): : 1 - 14
  • [25] PRECIPITATION AND DISSOLUTION KINETICS IN AL-LI-CU-MG ALLOY-8090
    LUO, A
    LLOYD, DJ
    GUPTA, A
    YOUDELIS, WV
    ACTA METALLURGICA ET MATERIALIA, 1993, 41 (03): : 769 - 776
  • [26] Evolution of texture and microstructure in a thermomechanically processed Al-Li-Cu-Mg alloy
    Singh, AK
    Saha, GG
    Gokhale, AA
    Ray, RK
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1998, 29 (02): : 665 - 675
  • [27] Low cycle fatigue behaviour of an underaged Al-Li-Cu-Mg alloy
    Prasad, NE
    Malakondaiah, G
    Rao, PR
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2004, 57 (02) : 181 - 194
  • [28] Role of constituent intermetallic phases and precipitates in initiation and propagation of intergranular corrosion of an Al-Li-Cu-Mg alloy
    Xu, X.
    Hao, M.
    Chen, J.
    He, W.
    Li, G.
    Li, K.
    Jiao, C.
    Zhong, X. L.
    Moore, K. L.
    Burnett, T. L.
    Zhou, X.
    CORROSION SCIENCE, 2022, 201
  • [29] Effect of electrolyte temperature on the polarization characteristics of an Al-Li-Cu-Mg alloy in NaOH
    Thakur, C
    Balasubramaniam, R
    BULLETIN OF MATERIALS SCIENCE, 1997, 20 (01) : 125 - 133
  • [30] LOCAL CHEMISTRY OF STRESS-CORROSION CRACKING IN AL-LI-CU-MG ALLOYS
    CRAIG, JG
    NEWMAN, RC
    JARRETT, MR
    HOLROYD, NJH
    JOURNAL DE PHYSIQUE, 1987, 48 (C-3): : 825 - 833
12345