HIGH TEMPERATURE CRUSHING STRENGTH OF VARIOUS IRON ORE PELLETS.

被引：0
|
作者：
Taniguchi, Shigeji
Ohmi, Munekazu
Yamamura, Eiji
机构：
来源：
Technology Reports of the Osaka University | 1982年 / 32卷 / 1652-1683期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The high-temperature crushing strength of iron ore pellets was measured in air atmosphere in the range from 600 to 100 degree C for eight types of self-fluxing pellets with basicities up to 2. 54 and slag contents up to 16. 3%, three kinds of acid pellets, and two kinds of pure hematite pellets with or without calcium silicate. The strength generally decreases as the tempeerature rises. However, the pellets containing silicate slags as major bonding phases showed a strength recovery, depending on the nature of the silicates. The temperature at which such strength recovery takes place varies with the composition of the silicate slag. An increase in the slag content enhanced the room temperature strength but it does not influence much the high-temperature strength.
引用
收藏
页码：213 / 220
相关论文
共 50 条
  • [31] Temperature patterns on hollow cylindrical catalytic pellets.
    Luss, D
    Annamalai, J
    ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 1999, 218 : U302 - U302
  • [32] EFFECTS OF GASEOUS SULFIDE ON THE REDUCTION OF IRON OXIDE PELLETS.
    Kuwano, Rokuro
    Oku, Takao
    Ono, Yoichi
    Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan, 1980, 66 (12): : 1622 - 1630
  • [33] Effect of TiO2 on compressive strength and microstructure of high basicity iron ore pellets
    Hu, Rong
    Li, Qi-di
    Ju, Jian-tao
    Li, Xin-yi
    Xiang, Xin-ru
    Yang, Xi-ming
    CANADIAN METALLURGICAL QUARTERLY, 2024, 63 (04) : 1643 - 1653
  • [34] THE VARIATION IN THE CRUSHING STRENGTH OF METALLIZED IRON PELLETS WITH BASICITY AFTER HYDROGEN REDUCTION
    TANIGUCHI, S
    OHMI, M
    TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1980, 21 (07): : 433 - 440
  • [35] Mechanical Testing of Pellets. Compressive Strength Determination.
    Meyers, Marc Andre
    Meyers, Pedro Paulo
    1600, (39):
  • [36] Study of Temperature Profile in the Induration of Magnetite Iron Ore Pellets
    Prusti, Pallishree
    Nayak, Bijaya Ketana
    Biswal, Surendra Kumar
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2017, 70 (02) : 453 - 462
  • [37] Influence of alkaline batch additives on the strength of iron-ore pellets
    Bersenev I.S.
    Bersenev E.S.
    Evstyugin S.N.
    Poluyakhtov R.A.
    Sudai A.V.
    Bersenev, I.S., 1600, Allerton Press Incorporation (44): : 588 - 589
  • [38] Influence of pore saturation on compressive strength of green iron ore pellets
    Sportel, H
    Droog, J
    IRONMAKING & STEELMAKING, 1997, 24 (03) : 221 - 223
  • [39] Effect of Flumag M Flux on Strength Properties of Iron Ore Pellets
    Kozhukhov A.A.
    Timofeeva A.S.
    Nikitchenko T.V.
    Steel in Translation, 2020, 50 (06) : 375 - 380
  • [40] Mechanisms of strength decrease in the initial reduction of iron ore oxide pellets
    Huang, Zhucheng
    Yi, Lingyun
    Jiang, Tao
    POWDER TECHNOLOGY, 2012, 221 : 284 - 291
12345