Corrosion-fatigue behaviour of Ti-75 titanium alloy

被引：0

作者：

Meng, Liang ^{[1
]}

Huan, Hong ^{[1
]}

Li, Zuochen ^{[1
]}

机构：

[1] Northwest Inst for Nonferrous Metal, Research, Baoji, China

来源：

Xiyou jinshu cailiao yu gongcheng | 1994年 / 23卷 / 03期

关键词：

Corrosion fatigue - Fatigue testing - Metallographic microstructure;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

An self-designed automatic liquor cycling unit for fatigue testing was introduced, and the experimental research of corrosion-fatigue properties of Ti-75 titanium alloy was carried out. The fatigue limits of 1×107 cycles determined in air and in 3.5wt% NaCl aqueous solution at room temperature are 392 MP and 431 MPa respectively. The results indicate that the corrosion-fatigue properties of Ti-75 alloy increase by a factor of 29% in air and 26% in 3.5wt% NaCl aqueous solution, as compared with TA5 alloy. The improvements of the properties shown above are related to the microstructure of Ti-75 alloy.

引用

页码：40 / 44

共 50 条

[41] Ti-75合金铸造后挠度的研究
张玉梅
郭天文
李佐臣
空军军医大学学报, 2000, (03) : 286 - 288
[42] EQUIPMENT FOR THE CORROSION-FATIGUE INVESTIGATION OF METALS
KUZUB, VS
GENERALOV, SV
NOVITSKII, VS
INDUSTRIAL LABORATORY, 1983, 49 (12): : 1289 - 1290
[43] CORROSION-FATIGUE BEHAVIOR OF METALLIC GLASSES
TANDON, KN
COLLINS, LE
CIM BULLETIN, 1986, 79 (890): : 68 - 68
[44] Corrosion-fatigue life of commercially pure titanium and Ti-6Al-4V alloys in different storage environments
Zavanelli, RA
Henriques, GEP
Ferreira, I
Rollo, JMDD
JOURNAL OF PROSTHETIC DENTISTRY, 2000, 84 (03): : 274 - 279
[45] CORROSION-FATIGUE CRACK INITIATION IN METALS
PATEL, C
PYLE, T
ROLLINS, V
NATURE, 1977, 266 (5602) : 517 - 518
[46] Corrosion, fatigue and corrosion fatigue behaviour of metal implant materials, especially titanium alloys
Fleck, Claudia
Eifler, Dietmar
INTERNATIONAL JOURNAL OF FATIGUE, 2010, 32 (06) : 929 - 935
[47] Corrosion-fatigue behavior of welded aluminum alloy 2024-T3
Yadav, V. K.
Gaur, V.
Singh, I. V.
INTERNATIONAL JOURNAL OF FATIGUE, 2023, 173
[48] ENVIRONMENTAL-EFFECTS ON CRACK CLOSURE IN THE CORROSION-FATIGUE OF AN ALUMINUM - LITHIUM ALLOY
PYUN, SI
CHUN, YG
CORROSION SCIENCE, 1993, 35 (1-4) : 611 - 619
[49] Corrosion-Fatigue in Steam Turbine Blades
Salzman, R. N.
Rieger, N. F.
Tschegg, S.
Schoenbauer, B.
Turnbull, A.
Zhou, S.
Gandy, D.
ADVANCES IN MATERIALS TECHNOLOGY FOR FOSSIL POWER PLANTS: PROCEEDINGS FROM THE SIXTH INTERNATIONAL CONFERENCE, 2010, 2011, : 450 - 469
[50] SPD INCREASES CORROSION-FATIGUE STRENGTH
NEMANOV, MS
RUSSIAN ENGINEERING JOURNAL-USSR, 1972, 52 (01): : 63 - &

← 1 2 3 4 5 →