Effects of cold expansion of a hole on fatigue crack initiation location and life of an LY12CZ alloy

被引：0
|
作者：
Chao, Ling [1 ]
Xiulin, Zheng [1 ]
机构：
[1] Hebei Inst of Technology, Tianjin, China
来源：
Fatigue and Fracture of Engineering Materials and Structures | 1992年 / 15卷 / 03期
关键词：
Cold Expansion - Fatigue Crack Initiation - LY12CZ Alloy;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：241 / 247
相关论文
共 50 条
  • [21] Mesoscopic study of ductile fracture of aluminium alloy LY12CZ
    Li, T
    Wang, QY
    Yuan, XM
    ADVANCES IN FRACTURE AND FAILURE PREVENTION, PTS 1 AND 2, 2004, 261-263 : 45 - 50
  • [22] Probabilistic Study on Corrosion Damage Distribution and Fatigue Lives of LY12CZ Aluminum Alloy Structure
    Yu, Dazhao
    Chen, Yueliang
    Yong, Zhang
    Fan Qinghe
    MECHANICAL, MATERIALS AND MANUFACTURING ENGINEERING, PTS 1-3, 2011, 66-68 : 594 - +
  • [23] Effect of cladding material on LY12CZ aluminium alloy by Laser Cladding
    Qingdao Branch, Naval Aeronautical Engineering Academy, Qingdao 266041, China
    Hanjie Xuebao, 2007, 10 (93-96):
  • [24] Influences of stress amplitude on the transient current behavior for LY12CZ aluminum alloy during corrosion fatigue
    Zhang, Bo
    Li, Jin
    Han, Enhou
    Ke, Wei
    Jinshu Xuebao/Acta Metallurgica Sinica, 2000, 36 (10): : 1089 - 1093
  • [25] Remaining Life Evaluation for LY12CZ Based on Non-linear Continuum Fatigue Damage Model
    Liang, Hua
    2020 5TH INTERNATIONAL CONFERENCE ON ELECTROMECHANICAL CONTROL TECHNOLOGY AND TRANSPORTATION (ICECTT 2020), 2020, : 308 - 311
  • [26] Study on the Initial Discontinuity State Distribution of LY12CZ Aluminum Alloy
    Han, Wei
    Yu, Dazhao
    Fan, Qinghe
    MATERIALS AND DESIGN, PTS 1-3, 2011, 284-286 : 1626 - 1629
  • [27] Infrared thermography for non-destructive evaluation of aluminum alloy LY12CZ under low cycle fatigue
    Li, Bin
    Tong, Xiaoyan
    Li, Zishan
    Cheng, Qiyou
    Yao, Leijiang
    TRANSFERABILITY AND APPLICABILITY OF CURRENT MECHANICS APPROACHES, 2009, : 483 - 487
  • [28] SEM in-situ study on pre-corrosion and fatigue cracking behavior of LY12CZ aluminum alloy
    Li Xudong
    Mu Zhitao
    Liu Zhiguo
    ADVANCES IN FRACTURE AND DAMAGE MECHANICS XI, 2013, 525-526 : 81 - 84
  • [29] Corrosion behavior of LY12CZ aluminum alloy in simulated acid rain solution
    An, BG
    Zhang, XY
    Song, SZ
    Li, HX
    Han, EH
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2003, 13 (01) : 116 - 120
  • [30] Corrosion behavior of LY12CZ aluminum alloy in simulated acid rain solution
    安百刚
    张学元
    宋诗哲
    李洪锡
    韩恩厚
    TransactionsofNonferrousMetalsSocietyofChina, 2003, (01) : 116 - 120
12345