INFLUENCE OF GRAPHITE FORM ON HYDRAULIC SOUNDNESS OF CAST IRON.

被引：0
|
作者：
Chernyshova, N.V.
Ezhov, G.I.
Boiko, G.G.
机构：
来源：
Soviet Castings Technology (English Translation of Liteinoe Proizvodstvo) | 1986年 / 02期
关键词：
CASTINGS - Physical Properties - STEEL TESTING - Fracture;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Comparative hydraulic soundness tests have been carried out on iron castings with different graphite forms, produced by the in-mold treatment process using 0. 2-1% of master alloy ZhKMK-4R, which contains 8. 3% Mg, 9. 2% Ca, 6. 7% REM, 47% Si, and remainder Fe. The original steelmaking pig iron contained 4. 13% C, 1. 05% Si, 1. 04% Mn, 0. 087% P, 0. 031% S, and melts were made in an acid-lined induction furnace of capacity 60 kg. The bath was heated to 1500 degree C and the molds were poured at 1450 degree C. The cylindrical castings - 30-mm diameter test bars of length 200 mm - were made in baked clay-bonded sand molds. The nodular graphite form ensures maximum hydraulic soundness.
引用
收藏
页码：31 / 32
相关论文
共 50 条
  • [1] Influence of Hypereutectic Graphite on the Solidification of Gray Cast Iron.
    Sun, G.X
    Loper Jr., C.R.
    Giessereipraxis, 1985, (07): : 89 - 95
  • [2] Influence of Graphite Nodularity on the Characteristics of Modified Cast Iron.
    Riposan, I.
    Boghici, M.
    Stefan, I.
    Cibian, S.
    Metalurgia Bucuresti, 1986, 38 (05): : 233 - 238
  • [3] GRAPHITE GROWTH IN CAST IRON.
    McSwain, R.H.
    Bates, C.E.
    AFS International Cast Metals Journal, 1976, 1 (01): : 53 - 57
  • [4] INFLUENCE OF GRAPHITIZING ADDITIVES ON FLAKE GRAPHITE CRYSTALLIZATION IN CAST IRON.
    Aleksandrov, N.N.
    Mil'man, B.S.
    Kapustina, L.S.
    1600,
  • [5] INFLUENCE OF SULFUR ON DISSOLVING BEHAVIOURS OF GRAPHITE IN MOLTEN CAST IRON.
    Kayama, Nobutaro
    Suzuki, Katsumi
    Report of the Castings Research Laboratory, Waseda University, 1979, (30): : 61 - 67
  • [6] AUSTENITIZING OF SPHEROIDAL GRAPHITE CAST IRON.
    Ueda, Yoshisada
    Wada, Noboru
    Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan, 1977, 63 (09): : 1572 - 1580
  • [7] FORMATION OF SPHEROIDAL GRAPHITE IN CAST IRON.
    Anikin, A.A.
    Kireev, N.N.
    Metal Science and Heat Treatment (English Translation of Metallovedenie i Termicheskaya Obrabotka, 1984, 26 (11-12): : 839 - 842
  • [8] GRAPHITE MORPHOLOGY CONTROL IN CAST IRON.
    Subramanian, S.V.
    Ghosh, Debu
    Kay, D.Alan R.
    Purdy, Gary R.
    I & SM, 1980, 7 (03): : 18 - 25
  • [9] Volume Increase of Nodular Graphite Cast Iron.
    Thury, Wolfgang
    Giesserei, 1976, 63 (18): : 506 - 509
  • [10] Microstructure and Properties of Vermicular Graphite Cast Iron.
    Nechtelberger, E.
    Lux, B.
    Giessereipraxis, 1984, (11): : 177 - 187
12345