Methodology of testing irradiated specimens for resistance to brittle fracture

被引：0
|
作者：
Vasnin, A.M. [1 ]
Garachuk, O.K. [1 ]
Karasev, V.S. [1 ]
Mamchich, S.D. [1 ]
Rivkin, E.Yu. [1 ]
Rodin, M.E. [1 ]
机构：
[1] Ukraine Academy of Sciences, Russia
来源：
Industrial laboratory | 1988年 / 54卷 / 04期
关键词：
Materials Testing - Fracture - Steel Testing - Crack Propagation;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Investigation of the influence of irradiation on the critical opening of the crack (COC) is performed on flat rectangular specimens with an edge crack for three-point bending tests which are fabricated from rolled steel 12KhGNMF. The radiation stability of this steel was estimated by results of tensile and shock bending tests. The influence of a different specimen irradiation temperature on the value of the critical crack opening was estimated during the tests. Specimens that were irradiated at the maximal (280°C) and minimal (240°C) temperatures were tested at identical temperatures. The data obtained showed that the difference in irradiation temperature in the 240-280°C range does not influence the resistance to brittle fracture for the steel 12KhGNMF.
引用
收藏
页码：517 / 520
相关论文
共 50 条
  • [21] Impact tensile fracture testing of a brittle polymer
    Arakawa, K.
    Mada, T.
    Todo, M.
    Takahashi, J.
    Ooka, S.
    POLYMER TESTING, 2006, 25 (08) : 1095 - 1100
  • [22] FRACTURE TESTING WITH SURFACE CRACK SPECIMENS
    ORANGE, TW
    JOURNAL OF TESTING AND EVALUATION, 1975, 3 (05) : 335 - 342
  • [23] FRACTURE MECHANICS AND NONDESTRUCTIVE TESTING OF BRITTLE MATERIALS
    CLARK, WG
    JOURNAL OF ENGINEERING FOR INDUSTRY, 1972, 94 (01): : 291 - &
  • [24] Fracture toughness and homogenity testing of brittle solids
    Lambrigger, M
    EUROMAT 97 - PROCEEDINGS OF THE 5TH EUROPEAN CONFERENCE ON ADVANCED MATERIALS AND PROCESSES AND APPLICATIONS: MATERIALS, FUNCTIONALITY & DESIGN, VOL 2: POLYMERS AND CERAMICS, 1997, : 407 - 410
  • [25] INFLUENCE OF PRELOADING ON BRITTLE-FRACTURE OF NOTCHED STEEL SPECIMENS
    NAKAMURA, M
    TSUYA, K
    TRANSACTIONS OF NATIONAL RESEARCH INSTITUTE FOR METALS, 1977, 19 (05): : 211 - 218
  • [26] Effect of residual stress on brittle fracture testing
    Hill, MR
    Panontin, TL
    FATIGUE AND FRACTURE MECHANICS: TWENTY-NINTH VOLUME, 1999, 1332 : 154 - 175
  • [27] A preliminary study on precursors of strong fracture in brittle material specimens
    Xu Jun
    Yang Run-Hai
    Zhang Jian-Guo
    Xu Zhao-Yong
    CHINESE JOURNAL OF GEOPHYSICS-CHINESE EDITION, 2011, 54 (09): : 2283 - 2292
  • [28] Fracture mechanics testing of irradiated RPV steels by means of sub-sized specimens: FRACTESUS project
    Cicero, S.
    Lambrecht, M.
    Swan, H.
    Arffman, P.
    Altstadt, E.
    Petit, T.
    Obermeier, F.
    Arroyo, B.
    Alvarez, J. A.
    Lacalle, R.
    1ST VIRTUAL EUROPEAN CONFERENCE ON FRACTURE - VECF1, 2020, 28 : 61 - 66
  • [29] FRACture mechanics TEsting of irradiated RPV steels by means of SUb-sized Specimens : FRACTESUS PROJECT
    Sanchez, Marcos
    Cicero, Sergio
    Arroyo, Borja
    Arrieta, Sergio
    23 EUROPEAN CONFERENCE ON FRACTURE, ECF23, 2022, 42 : 35 - 41
  • [30] NATURE OF FRACTURE-RESISTANCE IN STATIC AND IMPACT BEND TESTING OF SPECIMENS WITH A PRESSED NOTCH
    BELIK, AV
    DOLZHENKOV, FE
    NAVROTSKII, IV
    PILGUK, VE
    STRENGTH OF MATERIALS, 1982, 14 (01) : 137 - 140
12345