ANODIC POLARIZATION OF Fe-Cr BINARY ALLOYS EMBRITTLED AT 475 degree C and Fe-Cr COUPLING ELECTRODE IN N-H2SO4 SOLUTION.

被引：0
|
作者：
Mito, Masaji
Sugawara, Hideo
机构：
来源：
Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals | 1974年 / 38卷 / 01期
关键词：
IRON AND ALLOYS - Anodic Oxidation - IRON AND STEEL METALLOGRAPHY - Etching;
D O I：
10.2320/jinstmet1952.38.1_22
中图分类号：
学科分类号：
摘要：
Potentiodynamic polarization experiment was performed on a number of Fe-Cr binary alloys in N-H//2SO//4 solution with prolonged 475 degree C embrittlement. The curves for the Fe-Cr coupling electrode in which a high Cr alloy and a low Cr alloy were placed in a single mount were also studied. The second anodic current maximum in the active region was observed on embrittled (475 degree C multiplied by 1000 hr) 26% Cr alloy and 31% Cr alloy. Pronounced first peak and second peak potentials accorded with the passivation potentials for unembrittled 50% Cr, 15% Cr alloy, respectively. Behavior of the Fe-Cr coupling electrode resembled embrittled Fe-Cr alloys.
引用
收藏
页码：22 / 28
相关论文
共 50 条
  • [31] STRAINING ELECTRODE BEHAVIOR OF FE-CR AND NI-CR ALLOYS IN HIGH-TEMPERATURE AND HIGH-PRESSURE BORATE BUFFER SOLUTION
    SHIBATA, T
    FUJIMOTO, S
    TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1987, 28 (05): : 424 - 433
  • [32] Hot Corrosion of Fe-Cr Alloys with 75 Na2SO4+25 NaCl Coating at 1173 K
    Fu, Guangyan
    Tang, Xiaopeng
    Liu, Qun
    Su, Yong
    Wang, Xiao
    HIGH TEMPERATURE MATERIALS AND PROCESSES, 2012, 31 (06) : 717 - 721
  • [33] Metal dusting, carburization and diamond deposition on Fe-Cr alloys in CH4-H2 plasma atmospheres
    Sun, X.
    Ma, H. T.
    Yang, L. Z.
    Sanchez-Pasten, M.
    Penner, D. Craig
    Li, Y. S.
    Yang, Q.
    CORROSION SCIENCE, 2015, 98 : 619 - 625
  • [34] Accelerated degradation of Fe-Cr alloys induced by HCl and H2S in reducing atmospheres at 700 °C
    Pan Taijun
    Lu Weiming
    Zeng Chaoliu
    Niu Yan
    ACTA METALLURGICA SINICA, 2007, 43 (12) : 1261 - 1267
  • [35] PERIODIC PRECIPITATION OF SUBSCALE ON FE-CR ALLOYS OXIDIZED IN AR-H2O ATMOSPHERE
    KUSABIRAKI, K
    TOKI, H
    ASAMI, K
    OOKA, T
    TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1987, 27 (05) : B160 - B160
  • [36] Effect of Mn on oxide formation by Fe-Cr and Fe-Cr-Ni alloys in dry and wet CO2 gases at 650 °C
    Thuan Dinh Nguyen
    Zhang, Jianqiang
    Young, David J.
    CORROSION SCIENCE, 2016, 112 : 110 - 127
  • [37] PERIODIC PRECIPITATION OF SUBSCALE ON FE-CR ALLOYS OXIDIZED IN AR-H2O ATMOSPHERE
    KUSABIRAKI, K
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1986, 72 (13): : 1483 - 1483
  • [38] Effects of cerium and manganese on corrosion of Fe-Cr and Fe-Cr-Ni alloys in Ar-20CO2 gas at 818°C
    Thuan Dinh Nguyen
    Zhang, Jianqiang
    Young, David J.
    CORROSION SCIENCE, 2013, 76 : 231 - 242
  • [39] Water Vapor Effects on Corrosion of Fe-Cr and Fe-Cr-Ni Alloys Containing Silicon in CO2 Gas at 818 A°C
    Thuan Dinh Nguyen
    Zhang, Jianqiang
    Young, David J.
    OXIDATION OF METALS, 2015, 83 (5-6): : 575 - 594
  • [40] Corrosion behaviors of Fe-Cr alloys induced by KCl and KCl-ZnCl2 at 450°C
    Li, YS
    Niu, Y
    Wu, WT
    ACTA METALLURGICA SINICA, 2001, 37 (09) : 961 - 964
12345