Fatigue of Glass-epoxy Angle-plied Tubes under Cyclic Load.

被引：0
|
作者：
Ryska, Jaromir
机构：
来源：
Stavebnicky casopis | 1980年 / 28卷 / 11期
关键词：
COMPOSITE MATERIALS - FATIGUE OF MATERIALS - STRESSES - Analysis;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Fatigue behavior of fiberglass composite was studied by loading of plied tubes. The clear diameter of the tubes was 50 mm, their length 550 mm and their thickness ranged from 2 to 3 mm. Two series of specimens were tested.
引用
收藏
页码：827 / 837
相关论文
共 50 条
  • [41] Damage characterization of stiffened glass-epoxy laminates under tensile loading with acoustic emission monitoring
    Arumugam, V.
    Saravanakumar, K.
    Santulli, C.
    COMPOSITES PART B-ENGINEERING, 2018, 147 : 22 - 32
  • [42] Glass reinforced epoxy tubes subjected to indentation load: A study of scaling effects
    Hafeez, F.
    Almaskari, F.
    COMPOSITE STRUCTURES, 2014, 117 : 433 - 444
  • [43] ACCUMULATION OF AXIAL STRAIN OF A CYLINDRICAL BAR UNDER COMBINED CYCLIC TORSION AND AXIAL LOAD.
    Inoue, Kunio
    Nakagawa, Kenji
    Fujiyama, Masami
    Technology Reports of the Osaka University, 1976, 26 (1276-1307): : 223 - 231
  • [44] FAILURE ANALYSIS OF WOVEN GLASS-EPOXY PREPREG BOLTED JOINTS UNDER DIFFERENT CLAMPING MOMENTS
    Esendemir, Uemran
    ADVANCED COMPOSITES LETTERS, 2008, 17 (05) : 165 - 175
  • [45] FATIGUE OF MINERAL GLASS UNDER STATIC AND CYCLIC LOADING
    GURNEY, C
    PEARSON, S
    PROCEEDINGS OF THE ROYAL SOCIETY OF LONDON SERIES A-MATHEMATICAL AND PHYSICAL SCIENCES, 1948, 192 (1031): : 537 - 544
  • [46] Experimental Failure Analysis of Glass-Epoxy Laminated Composite Bolted-Joints with Clearance Under Preload
    Sen, Faruk
    Pakdil, Murat
    Sayman, Onur
    Benli, Semih
    INTERNATIONAL JOURNAL OF DAMAGE MECHANICS, 2011, 20 (02) : 163 - 178
  • [47] Effects of the number of fatigue cycles on the impact behavior of glass fiber/epoxy composite tubes
    Kara, Memduh
    Kirici, Muhammed
    COMPOSITES PART B-ENGINEERING, 2017, 123 : 55 - 63
  • [48] Bending Strength of Silicon Nitride at 1250 degree C under Static and Cyclic Bending Load.
    Helmuth Heigl
    Heckel, Klaus
    CFI Ceramic Forum International, 1983, 60 (2-3): : 69 - 73
  • [49] Fatigue characteristics of ancient brick masonry under cyclic load
    Xia, Qian
    Guo, Chaoxia
    Li, Yiqing
    Liu, Taikang
    Liu, Junjun
    CONSTRUCTION AND BUILDING MATERIALS, 2023, 400
  • [50] Failure analysis of graphite/epoxy filament wound tubes under cyclic loading
    Masudi, H
    Green, J
    PROCEEDINGS OF THE 10TH (2000) INTERNATIONAL OFFSHORE AND POLAR ENGINEERING CONFERENCE, VOL IV, 2000, : 66 - 71
12345