Fatigue of Glass-epoxy Angle-plied Tubes under Cyclic Load.

被引：0
|
作者：
Ryska, Jaromir
机构：
来源：
Stavebnicky casopis | 1980年 / 28卷 / 11期
关键词：
COMPOSITE MATERIALS - FATIGUE OF MATERIALS - STRESSES - Analysis;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Fatigue behavior of fiberglass composite was studied by loading of plied tubes. The clear diameter of the tubes was 50 mm, their length 550 mm and their thickness ranged from 2 to 3 mm. Two series of specimens were tested.
引用
收藏
页码：827 / 837
相关论文
共 50 条
  • [1] TENSILE CREEP OF ANGLE-PLIED BORON-EPOXY LAMINATES
    CHWIRUT, DJ
    JOURNAL OF TESTING AND EVALUATION, 1975, 3 (06) : 442 - 448
  • [2] Plastic instability of angle-plied cylindrical shells under biaxial tension
    Zinov'ev, P.A.
    Tsvetkov, S.V.
    Mekhanika Kompozitnykh Materialov, 1994, 30 (05): : 652 - 663
  • [3] Fatigue damage evolution in unidirectional glass/epoxy composites under a cyclic load
    Castro, Oscar
    Carraro, Paolo Andrea
    Maragoni, Lucio
    Quaresimin, Marino
    POLYMER TESTING, 2019, 74 : 216 - 224
  • [4] Hydrothermal fatigue on interface of glass-epoxy laminates
    Ray, BC
    JOURNAL OF REINFORCED PLASTICS AND COMPOSITES, 2005, 24 (10) : 1051 - 1056
  • [5] Fatigue behaviour of aged glass-epoxy composites
    Vauthier, E
    Chateauminois, A
    Bailliez, T
    PROGRESS IN DURABILITY ANALYSIS OF COMPOSITE SYSTEMS, 1996, : 159 - 165
  • [6] Damage and fracture by delamination in a glass-epoxy composite under static and cyclic loading
    Laksimi, A.
    Cherfaoui, M.
    Materiaux et Techniques, 1988, 76 (06): : 23 - 30
  • [7] Failure behaviour of the single lap joints of angle-plied composites under three point bending tests
    Kadioglu, Ferhat
    Demiral, Murat
    JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, 2020, 34 (05) : 531 - 548
  • [8] FATIGUE-CRACK INITIATED FROM A NOTCH TIP UNDER A CYCLIC COMPRESSIVE LOAD.
    Liu, Tianhua
    Chu, Wuyang
    Xiao, Jimei
    Jin, Lianqiang
    1600, (20):
  • [9] Cyclic water absorption behavior of glass-vinylester and glass-epoxy composites
    Alvarez, V.
    Vazquez, A.
    De La Osa, O.
    JOURNAL OF COMPOSITE MATERIALS, 2007, 41 (10) : 1275 - 1289
  • [10] Fatigue behaviour and damage mechanisms under strain controlled cycling: Comparison of Flax-epoxy and Glass-epoxy composites
    Mahboob, Zia
    Fawaz, Zouheir
    Bougherara, Habiba
    COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2022, 159
12345