EFFECT OF RESIDUAL HYDROGEN CONTENT ON COLD CRACK SUSCEPTIBILITY IN WELD METAL OF HIGH STRENGTH STEELS.

被引：0
|
作者：
Matsda, Fukuhisa
Nakagawa, Hiroji
Shinozaki, Kenji
Takaba, Shinji
Kihara, Hiroshi
机构：
来源：
Transactions of JWRI (Japanese Welding Research Institute) | 1981年 / 10卷 / 02期
关键词：
WELDS - Mechanical Properties;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The residual hydrogen content was measured in the LB - TRC (Longitudinal Bead-Tensile Restraint Cracking) test specimens. The relationship between the residual hydrogen content and the lower critical stress was investigated using commerical high strength steels. The lower critical stress strongly depended on the residual hydrogen content in the weld metal.
引用
收藏
页码：55 / 63
相关论文
共 50 条
  • [21] Study of Residual Austenite Stability in High-Strength Stainless Steels.
    Voronenko, B.I.
    Zemlyanikin, V.F.
    Makhnev, E.S.
    Izvestiya Vysshikh Uchebnykh Zavedenij. Chernaya Metallurgiya, 1982, (02): : 59 - 63
  • [22] DEVELOPMENT OF CONTINUOUSLY ANNEALED HIGH STRENGTH COLD ROLLED SHEET STEELS.
    Araki, Kenji
    Fukunaka, Shiro
    Uchida, Kuniki
    1977, 17 (12): : 701 - 709
  • [23] EFFECT OF OXYGEN ON HYDROGEN CRACKING IN HIGH-STRENGTH WELD METAL
    SHINOZAKI, K
    WANG, X
    NORTH, TH
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1990, 21 (05): : 1287 - 1298
  • [24] HYDROGEN-INDUCED CRACKING SUSCEPTIBILITY IN HIGH-STRENGTH WELD METAL.
    Okuda, N.
    Ogata, Y.
    Nishikawa, Y.
    Aoki, T.
    Goto, A.
    Abe, T.
    Welding Journal (Miami, Fla), 1987, 66 (05):
  • [25] Susceptibility of low strength rutile flux-cored weld metal to hydrogen assisted cold cracking
    Pitrun M.
    Nolan D.
    Welding in the World, 2006, 50 (5-6) : 24 - 37
  • [26] Influence of the Inclusions' Content and Form on the Cold Cracking Susceptibility of C-Mn Steels.
    Governatori, G.
    Cavagna, M.
    Rivista Italiana della Saldatura, 1976, 28 (02): : 97 - 104
  • [27] THE EFFECT OF HYDROGEN ON CRACK INITIATION IN BAINITE AND MARTENSITE IN HIGH-STRENGTH STEELS
    SISAK, W
    THOMPSON, AW
    JOURNAL OF METALS, 1983, 35 (08): : A7 - A7
  • [28] Influence of Weld Repair by Gouging on the Residual Stresses in High Strength Steels
    Kromm, Arne
    Schasse, Rene
    Xu, Ping
    Mente, Tobias
    Kannengiesser, Thomas
    RESIDUAL STRESSES 2016: ICRS-10, 2017, 2 : 169 - 174
  • [29] MACROSCOPIC AND MICROSCOPIC PROCESSES IN THE DELAYED FRACTURE CRACK GROWTH OF HIGH STRENGTH STEELS.
    Aoki, Takao
    Kanao, Masao
    Araki, Toru
    Transactions of National Research Institute for Metals (Tokyo), 1982, 24 (01): : 1 - 9
  • [30] Identification of Weld Residual Stresses Using Diffraction Methods and their Effect on Fatigue Strength of High Strength Steels Welds
    Mraz, L'ubos
    Karlsson, Leif
    Mikula, Pavol
    Vrana, Miroslav
    INTERNATIONAL CONFERENCE ON RESIDUAL STRESSES 9 (ICRS 9), 2014, 768-769 : 668 - +
12345