High-temperature crack growth in monolithic and SiCw-reinforced silicon nitride under static and cyclic loads

被引：0
|
作者：
机构：
[1] Ramamurty, U.
[2] Hansson, T.
[3] Suresh, S.
来源：
Ramamurty, U. | 1600年 / American Ceramic Soc, Westerville, OH, United States卷 / 77期
关键词：
Ceramic materials - Composite materials - Crack propagation - Degradation - Fatigue of materials - Fracture - High temperature effects - Hot pressing - Loads (forces) - Silicon carbide - Stresses;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Experimental results are presented on subcritical crack growth under sustained and cyclic loads in a HIPed Si3N4 at 1450°C and a hot-pressed Si3N4-10 vol% SiCw composite at 1300-1400°C. Static and cyclic crack growth rates are obtained from the threshold for the onset of the stable fracture with different cyclic frequencies and load ratios. Electron microscopy of crack wake contact and crack-tip damage illustrate the mechanisms of subcritical crack growth under static and cyclic loading.
引用
收藏
相关论文
共 50 条
  • [41] High-temperature fatigue crack growth under transient overloading: application to Alloy 617
    Pribe, Joshua D.
    Addison, Dylan A.
    Siegmund, Thomas
    Kruzic, Jamie J.
    INTERNATIONAL JOURNAL OF FRACTURE, 2021, 232 (01) : 23 - 42
  • [42] High-temperature fatigue crack growth under transient overloading: application to Alloy 617
    Joshua D. Pribe
    Dylan A. Addison
    Thomas Siegmund
    Jamie J. Kruzic
    International Journal of Fracture, 2021, 232 : 23 - 42
  • [43] INVESTIGATIONS OF HIGH-TEMPERATURE DEFORMATION AND CRACK-GROWTH UNDER VARIABLE LOAD HISTORIES
    BRUST, FW
    INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 1995, 32 (15) : 2191 - &
  • [44] STUDY ON CYCLIC CRACK-GROWTH OF CARBON AND LOW-ALLOY STEEL IN HIGH-TEMPERATURE PURE WATER .1. EFFECTS OF TEMPERATURE AND DISSOLVED-OXYGEN CONTENT ON CYCLIC CRACK-GROWTH RATE IN HIGH-TEMPERATURE PURE WATER
    HIGUCHI, M
    SAKAMOTO, H
    TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1987, 27 (05) : B165 - B165
  • [45] Effect of microstructure on high-temperature compressive creep of self-reinforced hot-pressed silicon nitride
    Boling-Risser, MA
    Goretta, KC
    Routbort, JL
    Faber, KT
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2000, 83 (12) : 3065 - 3069
  • [46] Reactions of NH3 on high-temperature silicon surface and structure evolution during silicon nitride film growth
    Zang, Kan
    Niu, Tong
    Wang, Wei Han
    Dong, Huajun
    Guo, Fangzhun
    JAPANESE JOURNAL OF APPLIED PHYSICS, 2023, 62 (08)
  • [47] High-temperature slow crack growth of an Yb2O3-SiO2-doped hot-pressed silicon nitride ceramic
    Guo, SQ
    Hirosaki, N
    Yamamoto, Y
    Nishimura, T
    Tanaka, H
    MATERIALS LETTERS, 2003, 57 (21) : 3257 - 3264
  • [48] DETERMINATION OF THRESHOLD STRESS INTENSITY FOR CRACK-GROWTH AT HIGH-TEMPERATURE IN SILICON-CARBIDE CERAMICS
    MINFORD, EJ
    TRESSLER, RE
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1983, 66 (05) : 338 - 340
  • [49] Low Cycle Fatigue Crack Growth Behavior of Modified Rotor Steel under High-Temperature
    Si, J.
    Yan, Z. R.
    Luo, X. M.
    Xuan, F. Z.
    PRESSURE VESSEL TECHNOLOGY: PREPARING FOR THE FUTURE, 2015, 130 : 1066 - 1074
  • [50] EFFECT OF CONDITIONS OF SILICON MONOCRYSTALS GROWTH ON OXYGEN PRECIPITATION UNDER HIGH-TEMPERATURE TREATMENT
    PUZANOV, NI
    EIDENZON, AM
    KRISTALLOGRAFIYA, 1992, 37 (05): : 1244 - 1253
12345