COLD ROLLING AND RECRYSTALLIZATION TEXTURES OF HIGH-PURITY IRON.

被引：0

作者：

Nakamura, Takayuki

Fukutsuka, Toshiro

Yagi, Yoshiro

机构：

来源：

Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan | 1972年 / 58卷 / 14期

关键词：

IRON AND ALLOYS;

D O I：

10.2355/tetsutohagane1955.58.14_2025

中图分类号：

学科分类号：

摘要：

Zone melted iron specimens with different grain sizes (40 vs 270 mu ) were hot forged and hot rolled into 2 mm sheet, which was then further reduced to 0. 5 mm thickness by cold rolling 75%. This was followed by isothermal salt bath annealing at 500 or 575 C. The effect of grain boundaries on cold rolling and recrystallization textures was determined by x-ray pole figure measurements and optical and electron microscopy.

引用

页码：2025 / 2033

共 50 条

[21] EFFECT OF NITROGEN ON THE RECRYSTALLIZATION TEXTURE IN HIGH-PURITY IRON
OKAMOTO, A
MIZUI, N
TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1985, 25 (02) : B76 - B76
[22] EFFECT OF NITROGEN ON THE RECRYSTALLIZATION TEXTURE IN HIGH-PURITY IRON
OKAMOTO, A
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1984, 70 (13): : 1246 - 1246
[23] PREPARATION OF HIGH-PURITY IRON AND ITS RECRYSTALLIZATION TEMPERATURE
ISSHIKI, M
IGAKI, K
TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1977, 18 (05): : 412 - 422
[24] A MECHANISM FOR SECONDARY RECRYSTALLIZATION IN HIGH-PURITY SILICON IRON
WALTER, JL
ACTA METALLURGICA, 1959, 7 (06): : 424 - 426
[25] Recrystallization in high purity polycrystalline magnesium during cold rolling
Yamamoto, Atsushi
Jotoku, Masaya
Tsubakino, Harushige
SOLID-SOLID PHASE TRANSFORMATIONS IN INORGANIC MATERIALS 2005, VOL 1, 2005, : 635 - 640
[26] RECRYSTALLIZATION OF HIGH-PURITY COPPER AS A RESULT OF LOW-TEMPERATURE ROLLING
GINDIN, IA
LAZAREVA, MB
MATSEVIT.VM
STARODUB.YD
PHYSICS OF METALS AND METALLOGRAPHY-USSR, 1969, 28 (05): : 193 - &
[27] COMPARATIVE RECRYSTALLIZATION BEHAVIOUR OF SWAGED AND ROLLED HIGH-PURITY IRON
RICHARDS, CE
WATSON, TW
JOURNAL OF THE IRON AND STEEL INSTITUTE, 1969, 207 : 582 - &
[28] FORMATION OF ANNEALING TWINS DURING RECRYSTALLIZATION OF HIGH-PURITY IRON
VILTANGE, M
COMPTES RENDUS HEBDOMADAIRES DES SEANCES DE L ACADEMIE DES SCIENCES SERIE C, 1975, 280 (03): : 69 - 71
[29] INFLUENCE OF SMALL ADDITIONS OF ELEMENTS ON RECRYSTALLIZATION OF HIGH-PURITY IRON
GRABOVSK.VY
NATAPOV, BS
OLSHANET.VE
SHTEKHNO, ON
STEEL IN THE USSR, 1971, 1 (04): : 308 - &
[30] EFFECT OF HEAT TREATMENT PRIOR TO COLD ROLLING ON THE SECONDARY RECRYSTALLIZATION TEXTURE IN SILICON IRON.
Tseytlin, A.M.
Segal, V.M.
Kaletina, A.V.
Petrova, T.A.
Sov Mater Sci Rev, 1987, 1 (03): : 363 - 367

← 1 2 3 4 5 →