'Superplastic forming' of commercial purity aluminum

被引：0
|
作者：
Nanyang Technological Univ, Singapore [1 ]
机构：
来源：
Scripta Mater | / 1卷 / 145-148期
关键词：
Crystal microstructure - Etching - Metal forming - Optical microscopy - Sheet metal - Strain rate - Superplasticity;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The performance of commercial purity aluminum is compared with superplastic alloy following superplastic forming. It is indicated that using optimum cycle (strain rates), is it possible to superplastically form inexpensive commercial purity aluminum to the same extent as some of the commercially available superplastic alloy in a die with relatively simple configuration.
引用
收藏
相关论文
共 50 条
  • [1] Superplastic forming of commercial purity aluminum
    Patankar, SN
    Jen, TM
    SCRIPTA MATERIALIA, 1997, 38 (01) : 145 - 148
  • [2] SUPERPLASTIC FORMING OF A COMMERCIAL ALUMINUM-ALLOY
    TAVASSOLI, AA
    RAZAVI, SE
    FALLAH, NM
    METALLURGICAL TRANSACTIONS, 1975, A 6 (03): : 591 - 594
  • [3] Forming of Tubular Commercial Purity Aluminum by ECAP
    Valder, James
    Rijesh, M.
    Surendranathan, A. O.
    MATERIALS AND MANUFACTURING PROCESSES, 2012, 27 (09) : 986 - 989
  • [4] FORMING IN SUPERPLASTIC ALUMINUM
    SAWLE, R
    CME-CHARTERED MECHANICAL ENGINEER, 1978, 25 (11): : 73 - 75
  • [5] Commercial applications of superplastic forming
    Osada, K
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 1997, 68 (03) : 241 - 245
  • [6] SUPERPLASTIC FORMING OF 7475 ALUMINUM
    MAHONEY, MW
    HAMILTON, CH
    JOURNAL OF METALS, 1979, 31 (12): : 89 - 89
  • [7] Superplastic Forming of Aluminum.
    Whittaker, J.A.
    Werkstatt und Betrieb, 1976, 109 (09): : 513 - 515
  • [8] Superplastic forming of aluminum alloys
    Barnes, A.J.
    Materials Science Forum, 1994, 170-172 : 701 - 714
  • [9] Developing a superplastic forming capability in a commercial aluminum alloy without scandium or zirconium additions
    Lee, S
    Furukawa, M
    Horita, Z
    Langdon, TG
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 342 (1-2): : 294 - 301
  • [10] SUPERPLASTIC BEHAVIOR OF COMMERCIAL ALUMINUM BRONZE
    NAKATANI, Y
    OHNISHI, T
    HIGASHI, K
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1984, 48 (01) : 113 - 114
12345