Crack resistance of modern heat resistant nickel alloys under long-term static loading at elevated temperatures

被引：0
|
作者：
Vorob'ev, N.A.
机构：
来源：
Izvestia Akademii nauk SSSR. Metally | 1995年 / 02期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：131 / 138
相关论文
共 50 条
  • [21] Long-Term Crack Behavior under Creep and Creep-Fatigue Conditions of Heat Resistant Steels
    Scholz, A.
    Berger, C.
    Mueller, F.
    Klenk, A.
    ADVANCES IN MATERIALS TECHNOLOGY FOR FOSSIL POWER PLANTS, 2008, : 718 - +
  • [22] Calculation of the Lifetime of Heat and Power Equipment Under Long-Term Static Loading, High Temperature, and the Action of Hydrogen
    Ch. Shu
    О. V. Hembara
    О. Ya. Chepil’
    Materials Science, 2018, 54 : 107 - 114
  • [23] Microstructural evolution of Type 304 austenitic heat resistant steel after long-term creep exposure at the elevated temperatures
    Yamazaki, M
    Kimura, K
    Hongo, H
    Watanabe, T
    Irie, H
    CREEP AND FRACTURE OF ENGINEERING MATERIALS AND STRUCTURES, 2001, : 659 - 667
  • [24] Calculation of the Lifetime of Heat and Power Equipment Under Long-Term Static Loading, High Temperature, and the Action of Hydrogen
    Shu, Ch.
    Hembara, O. V.
    Chepil', O. Ya.
    MATERIALS SCIENCE, 2018, 54 (01) : 107 - 114
  • [25] CONDITIONS OF TRANSITION FROM INITIAL TO ACCELERATED STAGE OF SUBCRITICAL CRACK-GROWTH IN CAST HEAT-RESISTANT STEEL UNDER LONG-TERM LOADING
    GLADSHTEIN, VI
    SEMENOVA, TN
    STRENGTH OF MATERIALS, 1979, 11 (10) : 1144 - 1148
  • [26] Anisotropy of the Cyclic Crack Resistance of Aluminum Alloys After Long-Term Operation
    Andreiko, I. M.
    Holovatyuk, Yu. V.
    Ostash, O. P.
    Semenets', O. I.
    Koval'chuk, L. B.
    MATERIALS SCIENCE, 2016, 52 (01) : 83 - 88
  • [27] Anisotropy of the Cyclic Crack Resistance of Aluminum Alloys After Long-Term Operation
    I. M. Andreiko
    Yu. V. Holovatyuk
    O. P. Ostash
    O. I. Semenets’
    L. B. Koval’chuk
    Materials Science, 2016, 52 : 83 - 88
  • [28] Long-term failure of isotropic viscoelastic material with a crack under cyclic loading
    Selivanov, M.F.
    Prikladnaya Mekhanika, 1999, 35 (02): : 60 - 64
  • [29] LONG-TERM RUPTURE STRENGTH OF ALLOYS AND PLASTICS FROM TENSILE STRENGTH AT ELEVATED TEMPERATURES
    GOLDFEIN, S
    JOURNAL OF BASIC ENGINEERING, 1966, 88 (04): : 762 - &
  • [30] LONG-TERM RUPTURE STRENGTH OF ALLOYS AND PLASTICS FROM TENSILE STRENGTH AT ELEVATED TEMPERATURES
    GOLDFEIN, S
    MECHANICAL ENGINEERING, 1965, 87 (10) : 72 - &
12345