Characterization of oxide layers on Ti-2Al-2.5Zr and.Ti-4A1-2V alloys oxidized at 300 °C in a neutral water steam

被引：0
|
作者：
机构：
[1] Wang, Z.G.
[2] Zu, X.T.
[3] Lian, J.
[4] Huang, X.Q.
[5] Wang, L.
[6] 1,Liu, Y.Z.
[7] Wang, L.M.
来源：
Zu, X.T. (zuxt@sohu.com) | 1600年 / Elsevier Ltd卷 / 384期
关键词：
Auger electron spectroscopy - Diffusion - Oxidation - Raman spectroscopy - Scanning - Stream flow - Transmission electron microscopy - X ray diffraction;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Two new a-titanium alloys, Ti-2Al-2.5Zr and Ti-4A1-2V, have been oxidized at 300 C in a neutral water steam at a pressure of 8.5 MPa, and the oxidation behaviors were investigated using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), in situ auger electron spectroscopy (AES), Raman spectroscopy and cross-sectional transmission electron microscopy (TEM) techniques. The results showed that the oxide layer was mainly composed of anatase-TiO2, and the thickness of the oxide scales increased with oxidation time. TiO was found with increasing depth, and the segregation of Al at the surface was also found during oxidation process. © 2004 Eisevier B.V. All rights reserved.
引用
收藏
页码：1 / 2
相关论文
共 50 条
  • [31] 氢对Ti-2Al-2.5Zr钛合金疲劳性能的影响
    何晓
    沈保罗
    岳俊
    曹建玲
    邱绍宇
    邹红
    金属热处理, 2002, (12) : 10 - 13
  • [32] Precipitation of (Ti:V)(2)Al(C,N) in multiphase Al-Ti-V alloys
    Chang, WS
    Muddle, BC
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1996, 207 (01): : 64 - 71
  • [33] In-situ SEM:: Observation of monotonic and cyclic deformed structure in Ti-2Al-2.5Zr alloy
    Yu, ZT
    Zhou, LA
    Gu, HC
    Deng, J
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2001, 17 (01) : 37 - 38
  • [34] Ti-2Al-2.5Zr钛合金丝材的普通退火工艺
    王海波
    毛小南
    洪权
    热加工工艺, 2009, 38 (08) : 34 - 37
  • [35] Effect of grain size on twinning behavior in Ti-2Al-2.5Zr alloy fatigued at 77 K
    Wang, H.
    Sun, Q. Y.
    Xiao, L.
    Sun, J.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2012, 542 : 1 - 7
  • [36] Precipitation of (Ti,V)2Al(C,N) in multiphase Al-Ti-V alloys
    Chang, Woong-Seong
    Muddle, B.C.
    Materials Science and Engineering A, 1996, A207 (01) : 64 - 71
  • [37] Topography and thickness of passive layers on anodically oxidized Ti6Al4V alloys
    Szewczenko, Janusz
    Jaglarz, Janusz
    Basiaga, Marcin
    Kurzyk, Jan
    Skoczek, Edyta
    Paszenda, Zbigniew
    PRZEGLAD ELEKTROTECHNICZNY, 2012, 88 (12B): : 228 - 231
  • [38] Ti-2Al-2.5Zr合金再结晶特性及动力学机制
    于振涛
    周廉
    邓炬
    顾海澄
    稀有金属材料与工程, 1999, (06) : 340 - 344
  • [39] Ti-2Al-2.5Zr合金丝材延伸率影响因素分析
    羊玉兰
    王韦琪
    王建斌
    王小翔
    文志刚
    钛工业进展, 2006, (06) : 36 - 38
  • [40] Susceptibility to Pitting Corrosion of Ti-CP2, Ti-6Al-2Sn-4Zr-2Mo, and Ti-6Al-4V Alloys for Aeronautical Applications
    Jaquez-Munoz, Jesus
    Gaona-Tiburcio, Citlalli
    Lira-Martinez, Alejandro
    Zambrano-Robledo, Patricia
    Maldonado-Bandala, Erick
    Samaniego-Gamez, Oliver
    Nieves-Mendoza, Demetrio
    Olguin-Coca, Javier
    Estupinan-Lopez, Francisco
    Almeraya-Calderon, Facundo
    METALS, 2021, 11 (07)
12345