Damage-resistant SrO-doped Ce-TZP/Al2O3 composites

被引：0
|
作者：
Cutler, R.A. [1 ]
Lindemann, J.M. [1 ]
Ulvensoen, J.H. [1 ]
Lange, H.I. [1 ]
机构：
[1] Ceramatec, Inc, Salt Lake City, United States
来源：
Materials and Design | 1994年 / 15卷 / 03期
关键词：
Addition reactions - Alumina - Ceramic materials - Grinding (machining) - Low temperature effects - Micromachining - Microstructure - Powders - Residual stresses - Strength of materials - Strontium compounds;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Simultaneous additions of SrO and Al2O3 to ZrO2 (12 mol.% CeO2) lead to the in-situ formation of SrO&middot6Al2O3 platelets in the Al2O3/Ce-TZP matrix. These composites have superior damage resistance compared to Al2O3/Y-TZP ceramics despite their lower strength. The increased damage resistance appears to be primarily related to the higher residual stress as a result of grinding with smaller contributions due to micromechanical toughening. High damage resistance was also obtained by introduction of temperature-induced surface compressive stresses in layered composites. Damage resistance is only obtained at low temperatures (< 500°C). The applicability of conventional powder processing (slip casting or spray drying) to these tailored microstructures is demonstrated.
引用
收藏
页码：123 / 133
相关论文
共 50 条
  • [41] Purification of water from heavy metal of lead by nanocomposite of Ce-TZP/Al2O3
    Vahdat, Armin
    Ghasemi, Behrooz
    Yousefpour, Mardali
    INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2020, 17 (06) : 2563 - 2568
  • [42] (Ce-TZP)-Al2O3复合陶瓷摩擦磨损性能研究
    陈志刚
    陈昶
    朱贞祥
    硅酸盐通报, 1990, (04) : 9 - 16
  • [43] Synthesis and characterization of Ce-TZP/Al2O3 nanocomposites prepared via aqueous combustion
    Asadirad, M.
    Yoozbashizadeh, H.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2012, 514 : 150 - 156
  • [44] R-CURVE BEHAVIOR AND FLAW INSENSITIVITY OF CE-TZP/AL2O3 COMPOSITE
    RAMACHANDRAN, N
    CHAO, LY
    SHETTY, DK
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1993, 76 (04) : 961 - 969
  • [45] HRTEM observation of bonding interface between Ce-TZP/Al2O3 nanocomposite and porcelain
    Ban, Seiji
    Nawa, Masahiro
    Sugata, Fumio
    Tsuruki, Jiro
    Kono, Hiroshi
    Kawai, Tatsushi
    DENTAL MATERIALS JOURNAL, 2014, 33 (04) : 565 - 569
  • [46] Ce-TZP和Ce-TZP/Al2O3层状复合材料受载裂尖的相变特性
    卿新林
    贾晓东
    王国韬
    顾怡红
    戴福隆
    力学学报, 1997, (05) : 37 - 44
  • [47] Surface properties of Ce-TZP/Al2O3 composite ceramics by coating mesoporous bioactive glass
    Zhang, Yin
    Jiang, Feng
    Luan, Jiapan
    Zhou, Xiang
    Wu, Zhenning
    Li, Mingming
    Hong, Zhongrong
    COMPOSITES PART B-ENGINEERING, 2019, 164 : 499 - 507
  • [48] Toughness enhancement of Al2O3/Ce-TZP functionally graded materials by annealing in inert atmosphere
    Vleugels, J
    Zhao, C
    Van Der Biest, O
    FUNCTIONALLY GRADED MATERIALS VIII, 2005, 492-493 : 699 - 704
  • [49] Compositional dependence of hardness of (Ce,Y)-TZP/Al2O3 composites
    Gong, JH
    Miao, HZ
    Hu, BJ
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 372 (1-2): : 207 - 212
  • [50] Influences of ZrO2 nanoparticles on the microstructure and mechanical behavior of Ce-TZP/Al2O3 nanocomposites
    Gang Yang
    Junchu Li
    Gaochao Wang
    Masatomo Yashima
    Silin Min
    Journal of Materials Science, 2005, 40 : 6087 - 6090
12345