Gas-pressure sintering of β-silicon nitride containing Y2O3 and Nd2O3

被引：12
|
作者：
Hirosaki, Naoto
Ando, Motohide
Akimune, Yoshio
Mitomo, Mamoru
机构：
来源：
Nippon Seramikkusu Kyokai Gakujutsu Ronbunshi/Journal of the Ceramic Society of Japan | 1992年 / 100卷 / 1162期
关键词：
Doping (additives) - Firing (of materials) - Grain growth - Microstructure - Neodymium compounds - Oxides - Scanning electron microscopy - Sintering - Strength of materials - Yttrium compounds;
D O I：
10.2109/jcersj.100.826
中图分类号：
学科分类号：
摘要：
Y2O3-Nd2O3-doped β-Si3N4 was sintered at 1700°C to 1900°C for 4 h in 10 MPa N2, and the effect of the amount of the additives and sintering temperatures on strength, fracture toughness and the microstructure was investigated. A dense material (>98% of the theoretical) was obtained by firing at 1900°C with addition of 1 to 10 mol% of oxides. Rod-like β-Si3N4 grains developed by firing at 1900°C increased the fracture toughness up to 7.8 MPa √m because of the pull-out and the crack-deflection mechanism. The material made from β-Si3N4 powder had a high Weibull modulus than that from α-Si3N4 powder.
引用
收藏
页码：826 / 829
相关论文
共 50 条
  • [41] Thermodynamics and kinetics of sintering of Y2O3
    Nakajima, Kimiko
    Castro, Ricardo H. R.
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2020, 103 (09) : 4903 - 4912
  • [42] ANOMALOUS SINTERING BEHAVIOR OF Y2O3
    SCHIELTZ, JD
    WILDER, DR
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1967, 50 (08) : 439 - &
  • [43] Sintering behaviour of nanocrystalline Y2O3
    Merkert, P
    Hahn, H
    Rödel, J
    NANOSTRUCTURED MATERIALS, 1999, 12 (5-8): : 701 - 704
  • [44] Phase stability and mechanical properties of TZP with a low mixed Nd2O3/Y2O3 stabiliser content
    Xu, T
    Vleugels, J
    Van der Biest, O
    Kan, YM
    Wang, PL
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2006, 26 (07) : 1205 - 1211
  • [45] PHASE-EQUILIBRIA STUDIES IN THE TERNARY-SYSTEM AL2O3/Y2O3/ND2O3 USING ODTA
    CASLAVSKY, JL
    VIECHNICKI, D
    AMERICAN CERAMIC SOCIETY BULLETIN, 1982, 61 (08): : 808 - 808
  • [46] Fabrication of high thermal conductivity silicon nitride ceramics by pressureless sintering with MgO and Y2O3 as sintering additives
    Lu, Tao
    Wang, Tun
    Jia, Yingfei
    Ding, Maomao
    Shi, Ying
    Xie, Jianjun
    Lei, Fang
    Zhang, Lei
    Fan, Lingcong
    CERAMICS INTERNATIONAL, 2020, 46 (17) : 27175 - 27183
  • [47] Enhanced mechanical properties and in vitro bioactivity of silicon nitride ceramics with SiO2, Y2O3, and Al2O3 as sintering aids
    Han, Yongning
    Zhou, Wenying
    Li, Jian
    Han, Zhuoqun
    Bi, Lunan
    Zhang, Zheng
    Wang, Yang
    Li, Ling
    Zhao, Degang
    JOURNAL OF THE MECHANICAL BEHAVIOR OF BIOMEDICAL MATERIALS, 2025, 164
  • [48] Comparison of spectroscopic properties of neodymium-doped aluminium garnet (Nd:YAG) ceramics obtained by reactive sintering of Al2O3, Y2O3 and Nd2O3 and by synthesis of nanocrystalline Nd:YAG powders
    Kozlowska, Anna
    Nakielska, Magdalena
    Podniesinski, Dariusz
    Weglarz, Helena
    Wajler, Anna
    Librant, Zdzislaw
    Lukasiewicz, Tadeusz
    Malag, Andrzej
    OPTICAL COMPONENTS AND MATERIALS VIII, 2011, 7934
  • [49] Synthesis of Y2O3 and Y2O3:Nd3+ monodisperse crystalline nanospheres by homogenous precipitation
    Pazura, Yu, I
    Baumer, V. N.
    Deyneka, T. G.
    Vovk, O. M.
    Yavetskiy, R. P.
    FUNCTIONAL MATERIALS, 2010, 17 (01): : 107 - 113
  • [50] La2O3、Nd2O3、Y2O3对高岭石高温相变动力学的影响
    匡敬忠
    胡锦
    原伟泉
    材料导报, 2016, 30 (16) : 150 - 156+161
12345