Solidification, blowhole formation and cracking of steel weld metal

被引：0
|
作者：
Masumoto, I. [1 ]
机构：
[1] Japan Welding Soc, Japan
来源：
Welding Research Abroad | 1994年 / 40卷 / 11期
关键词：
Blowhole formation - Gamma phase solidification - Molten steel - Peritectic reaction;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：30 / 41
相关论文
共 50 条
  • [21] Weld Solidification Cracking in 304 to 304L Stainless Steel
    Hochanadel, P. W.
    Lienert, T. J.
    Martinez, J. N.
    Martinez, R. J.
    Johnson, M. Q.
    HOT CRACKING PHENOMENA IN WELDS III, 2011, : 145 - 160
  • [22] Computational analysis of thermal and mechanical conditions for weld metal solidification cracking
    Ohio State Univ, Columbus, United States
    Weld Res Abroad, 1 (34-41):
  • [23] Characteristics of reheat cracking in weld metal - study of reheat cracking in FCAW stainless steel weld metal (Report 1)
    Okazaki, Tsukasa
    Nishimoto, Kazutoshi
    Mori, Hiroaki
    Yosetsu Gakkai Ronbunshu/Quarterly Journal of the Japan Welding Society, 2000, 18 (01): : 59 - 67
  • [24] Weld solidification cracking in a 304L stainless steel water tank
    James, M. N.
    Matthews, L.
    Hattingh, D. G.
    ENGINEERING FAILURE ANALYSIS, 2020, 115
  • [25] WELD METAL SOLIDIFICATION
    SAVAGE, WF
    JOURNAL OF METALS, 1968, 20 (08): : A114 - &
  • [26] Effect of Nitrogen on Solidification Cracking Resistance in ERNiCr-3 Weld Metal
    Orr, M. R.
    Fink, C.
    Lippold, J. C.
    Argentine, F.
    WELDING JOURNAL, 2018, 97 (08) : 243S - 252S
  • [27] Numerical simulation of temperature fields for weld metal solidification cracking in stainless steels
    Wei, Yanhong
    Liu, Renpei
    Dong, Zujue
    Hanjie Xuebao/Transactions of the China Welding Institution, 1999, 20 (03): : 199 - 204
  • [28] Effect of weld travel speed on solidification cracking behavior. Part 1: weld metal characteristics
    N. Coniglio
    C. E. Cross
    The International Journal of Advanced Manufacturing Technology, 2020, 107 : 5011 - 5023
  • [29] IMPROVEMENT OF SOLIDIFICATION CRACKING SUSCEPTIBILITY OF ELECTRON BEAM WELD METAL OF FULLY AUSTENITIC TYPE 316 STAINLESS STEEL.
    Nakao, Yoshikuni
    Katsu, Shinichiro
    1600, (04):
  • [30] NUMERICAL SIMULATION OF TEMPERATURE FIELDS FOR WELD METAL SOLIDIFICATION CRACKING IN STAINLESS STEELS
    R. P. Liu
    Z. J. Dong and Y. H. Wei( 1)Harbin Research Institute of Welding
    Acta Metallurgica Sinica(English Letters), 2000, (01) : 139 - 144
12345