Characterization of superconducting (Tl,Bi)Sr2CaCu2Oy

被引：0
|
作者：
Superconductivity Technology Cent, Los Alamos, United States [1 ]
机构：
来源：
Phys C Supercond | / 3-4卷 / 358-364期
关键词：
Bismuth compounds - Calcium compounds - Composition effects - Magnetic hysteresis - Magnetic permeability - Oxide superconductors - Phase transitions - Strontium compounds - Superconducting transition temperature - Thallium compounds - X ray powder diffraction;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The superconducting phase with mixed Tl and Bi, namely (Tl0.55Bi0.45)Sr2CaCu2Oy, was synthesized and characterized. Synthesis conditions were studied, and this phase, (Tl,Bi)-1212, was found to form preferentially to (Tl,Bi)-1223 when Sr was present with no Ba present. X-ray powder diffraction with Rietveld refinement provided structural data. The phase is tetragonal with a = 3.7988(4) A and c = 12.076(1) A, with space group symmetry P4/mmm, and with a platelet crystal morphology. Magnetic-susceptibility data gave an onset of superconductivity Tc at 94.9 ± 1.3 K with a Tcmid of 86.0 ± 1.1 K. Magnetic-hysteresis measurements showed that substantial flux pinning occurs in this phase at high temperatures.
引用
收藏
相关论文
共 50 条
  • [41] CRITICAL CURRENT AS A FUNCTION OF TEMPERATURE IN SUPERCONDUCTING SINGLE-CRYSTAL (BI,PB)2SR2CACU2OY
    OYA, G
    AOYAMA, N
    KISHIDA, S
    TOKUTAKA, H
    PHYSICA C, 1991, 185 : 2453 - 2454
  • [42] SOLIDIFICATION OF BI2SR2CACU2OY AND BI2SR1.75CA0.25CUOY
    HOLESINGER, TG
    MILLER, DJ
    VISWANATHAN, HK
    CHUMBLEY, LS
    JOURNAL OF MATERIALS RESEARCH, 1993, 8 (09) : 2149 - 2161
  • [43] Fabrication and superconducting properties of Bi2Sr2CaCu2Oy multilayer tape prepared by continuous heat treatment
    Hasegawa, T
    Hikichi, Y
    Kumakura, H
    Kitaguchi, H
    Togano, K
    JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS & EXPRESS LETTERS, 1995, 34 (12B): : L1638 - L1640
  • [44] Non-conservation of density of states in Bi2Sr2CaCu2Oy:: Coexistence of pseudogap and superconducting gap
    Gupta, AK
    Ng, KW
    EUROPHYSICS LETTERS, 2002, 58 (06): : 878 - 884
  • [45] Fabrication and superconducting properties of Bi2Sr2CaCu2Oy multilayer tape prepared by continuous heat treatment
    Showa Electric Wire & Cable Co, Ltd, Kanagawa, Japan
    Jpn J Appl Phys Part 2 Letter, 12 B (L1638-L1640):
  • [46] INFLUENCE OF ALUMINUM AND INDIUM ADDITION ON THE PROPERTIES OF SUPERCONDUCTING BI2SR2CACU2OY METAL-OXIDE
    GOLOLOBOV, EM
    PRYTKOVA, NA
    TOMILO, ZM
    TURTSEVICH, DM
    TSELUEVSKII, MS
    SHIMANSKAYA, NM
    PHYSICA STATUS SOLIDI A-APPLIED RESEARCH, 1989, 115 (01): : K79 - K82
  • [47] EFFECTS ON TC AND JC IN THE (TL0.5PB0.5)SR2CACU2OY SUPERCONDUCTOR OF PARTIAL DOPING OF CA SITES BY NATURAL MISCHMETAL OXIDES
    JOHNSON, JD
    LIU, RS
    EDWARDS, PP
    CAMPBELL, AM
    WU, PT
    SOLID STATE COMMUNICATIONS, 1991, 77 (01) : 53 - 55
  • [48] IODINE AND LITHIUM INTERCALATION INTO THE HIGH-T(C) SUPERCONDUCTING OXIDE BI2SR2CACU2OY
    OHASHI, M
    GLOFFKE, W
    WHITTINGHAM, MS
    SOLID STATE IONICS, 1992, 57 (3-4) : 183 - 187
  • [49] Neutron Fluence Dependence of Superconducting Properties and Crystal Structure on Bi2Sr2CaCu2Oy Single Crystal
    Kusagaya, K.
    Terai, T.
    Chikumoto, N.
    Kobayashi, T.
    Shimoyama, J.
    Kishio, K.
    PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 1994, 235-40 : 2975 - 2976
  • [50] Phase transformation in Bi2Sr2CaCu2Oy single crystals
    Yang, G
    Shang, P
    Jones, IP
    Abell, JS
    Gough, CE
    ELECTRON MICROSCOPY AND ANALYSIS 1995, 1995, 147 : 441 - 444
12345