CRACK GROWTH RATE ANALYSIS IN PWR REACTOR PIPING.

被引：0
|
作者：
Doyen, J.J.
Lebey, M.
Vrillon, M.
机构：
来源：
Struct Anal of React Core and Coolant Circuit Struct | 1977年 / F卷
关键词：
NUCLEAR REACTORS; PRESSURIZED WATER - Cooling Systems - STAINLESS STEEL - Crack Propagation;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
This paper discusses the Aquitaine-1 program, an investigation into crack growth in PWR primary circuit piping. The experimental part of the program includes characterization of piping material, measurement of cracking speed, and an evaluation of cycling frequency. Three measurement methods for the crack depths are simultaneously utilized: a method by electrical potential, ultrasonic technics (Rayleigh waves, transversal waves). The comparison is made between the experimental results on the one hand the forecastings of growth speed resulting from the characterization of material and calculations of fracture mechanics on the other hand.
引用
收藏
相关论文
共 50 条
  • [21] Crack Growth Rate Analysis of Stress Corrosion Cracking
    Alkateb, Mohamed
    Tadic, Srdan
    Sedmak, Aleksandar
    Ivanovic, Ivana
    Markovic, Svetislav
    TEHNICKI VJESNIK-TECHNICAL GAZETTE, 2021, 28 (01): : 240 - 247
  • [22] Fracture analysis of the set-in nozzle of a PWR reactor pressure vessel - Part 1: Determination of critical crack
    Murtaza, Usman Tariq
    Hyder, M. Javed
    ENGINEERING FRACTURE MECHANICS, 2018, 192 : 343 - 361
  • [23] Statistical analysis methods of fatigue crack growth rate
    Zhang X.
    Xie L.
    Liu J.
    Zhang Y.
    Tong A.
    Ma Y.
    Transactions of Tianjin University, 2014, 20 (5) : 322 - 327
  • [24] Fatigue crack growth rate analysis in a titanium alloy
    Korsunsky, Alexander M.
    Dini, Daniele
    Walsh, Michael J.
    ADVANCES IN FRACTURE AND DAMAGE MECHANICS VII, 2008, 385-387 : 5 - +
  • [25] Statistical Analysis Methods of Fatigue Crack Growth Rate
    张啸尘
    谢里阳
    刘建中
    张宇
    佟安时
    马园园
    Transactions of Tianjin University, 2014, (05) : 322 - 327
  • [26] Statistical Analysis Methods of Fatigue Crack Growth Rate
    张啸尘
    谢里阳
    刘建中
    张宇
    佟安时
    马园园
    Transactions of Tianjin University, 2014, 20 (05) : 322 - 327
  • [27] SCC CRACK GROWTH RATE OF ALLOY 82 IN PWR PRIMARY WATER CONDITIONS - EFFECT OF A THERMAL TREATMENT l -
    Guerre, C.
    Duhamel, C.
    Sennour, M.
    Crepin, J.
    Le Calvar, M.
    15TH INTERNATIONAL CONFERENCE ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS-WATER REACTORS, 2011, : 1127 - 1139
  • [28] Crack growth behavior of nickel alloy welds in a PWR environment
    Alexandreanu, B.
    Chopra, O. K.
    Shack, W. J.
    PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE 2007, VOL 1: CODES AND STANDARDS, 2007, 1 : 201 - 212
  • [29] Analysis of crack growth rate based on rotation at the crack tip plastic zone
    A. Bhattacharya
    International Journal of Fracture, 1997, 83 : 159 - 165
  • [30] Analysis of crack growth rate based on rotation at the crack tip plastic zone
    Bhattacharya, A
    INTERNATIONAL JOURNAL OF FRACTURE, 1997, 83 (02) : 159 - 165
12345