ELECTROCHEMICAL STUDY ON EROSION-CORROSION OF CARBON STEEL AND STAINLESS STEEL.

被引：0
|
作者：
Umemura, Fumio [1 ]
Matukura, Shinji [1 ]
Kawamoto, Teruaki [1 ]
机构：
[1] Ishikawajima-Harima Heavy Industries, Co, Ishikawajima-Harima Heavy Industries Co
来源：
Boshoku gijutsu | 1987年 / 36卷 / 10期
关键词：
CORROSION PROTECTION; CATHODIC - ELECTROCHEMISTRY - HYDROGEN ION CONCENTRATION - STAINLESS STEEL - Corrosion - STEEL CORROSION;
D O I：
10.3323/jcorr1974.36.10_627
中图分类号：
学科分类号：
摘要：
Erosion corrosion behavior of a carbon steel and a stainless steel was studied by electrochemical measurements in jet-in-slit sand erosion testing. The test was conducted under the conditions of slurry flow rates lower than 5 m/s, pH range 1. 5-7. 0 and alumina particles of 4 multiplied by 10** minus **5 m diameter. The erosion corrosion rate is evaluated in terms of the corrosion rate obtained by electrochemical measurement and the erosion rate. The rate of the carbon steels is 15-300 times higher than that of the stainless steel. Under cathodic protection, the rate decreases, resulting in about the same rate as the stainless steel.
引用
收藏
页码：627 / 635
相关论文
共 50 条
  • [41] ON THE INITIATION OF CORROSION ON CARBON STEEL.
    Eklund, Goran
    1600, (01):
  • [42] Effect of Co on the corrosion resistance and erosion-corrosion behavior of duplex stainless steel surfacing layer
    Bao, Yefeng
    Wei, Shangzhi
    Liu, Yu
    Jiang, Yongfeng
    Yang, Ke
    Song, Qining
    WELDING IN THE WORLD, 2024, 68 (11) : 2985 - 2994
  • [43] CORROSION PERFORMANCE OF CARBON STEEL.
    Kirby, Gary N.
    Chemical Engineering (New York), 1979, 86 (06): : 72 - 84
  • [44] Electrochemical noise analysis of polyurethane-coated steel subjected to erosion-corrosion
    Puget, Y
    Trethewey, K
    Wood, RJK
    WEAR, 1999, 233 : 552 - 567
  • [45] Comparison of erosion, corrosion and erosion-corrosion of carbon steel in fluid containing micro- and nanosize particles
    Rashidi, A. M.
    Paknezhad, M.
    Mohamadi-Ochmoushi, M. R.
    Moshrefi-Torbati, M.
    TRIBOLOGY-MATERIALS SURFACES & INTERFACES, 2013, 7 (03) : 114 - 121
  • [46] Flow accelerated corrosion and erosion-corrosion behavior of marine carbon steel in natural seawater
    Xu, Yunze
    Zhang, Qiliang
    Zhou, Qipiao
    Gao, Shan
    Wang, Bin
    Wang, Xiaona
    Huang, Yi
    NPJ MATERIALS DEGRADATION, 2021, 5 (01)
  • [47] Effect of nitrogen addition on microstructure and erosion-corrosion behavior of stainless steel in acidic slurry
    Ping, Li
    Zhou, Cai Qi
    Kang, Wei Bo
    Jun, Li Feng
    CHINA FOUNDRY, 2009, 6 (03) : 197 - 201
  • [48] Investigations of Microstructures and Erosion-Corrosion Performance of Cast Boron-Bearing Stainless Steel
    Yi, Dawei
    Li, Bin
    Tan, Xiao
    Liu, Sifan
    Chen, Jin
    Li, Yefei
    COATINGS, 2021, 11 (12)
  • [49] Erosion-corrosion of 2205 duplex stainless steel in flowing seawater containing sand particles
    Hussain, E. A. M.
    Robinson, M. J.
    CORROSION SCIENCE, 2007, 49 (04) : 1737 - 1754
  • [50] Effect of nitrogen addition on microstructure and erosion-corrosion behavior of stainless steel in acidic slurry
    Li Ping 1-3
    2. School of Materials Science and Engineering
    3. China Yituo Group Co.
    ChinaFoundry, 2009, 6 (03) : 197 - 201
12345