Effect of H3BO3 doping and coating on the sintering and dielectric properties of BZN ceramics

被引：0
|
作者：
Jin, Biao [1 ]
Wang, Xiao [1 ]
Yang, Liu-Shuan [1 ,2 ]
机构：
[1] School of Civil Engineering, Henan University of Urban Construction, Pingdingshan 467036, China
[2] School of Material Science and Engineering, Henan University of Science and Technology, Luoyang 471003, China
来源：
Rengong Jingti Xuebao/Journal of Synthetic Crystals | 2014年 / 43卷 / 05期
关键词：
Bismuth compounds - Coatings - II-VI semiconductors - Liquids - Dielectric properties of liquids - Temperature - Zinc oxide - Ceramic materials - Niobium oxide;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
(Bi1.5Zn0.5) (Zn0.5Nb1.5)O7(BZN) main phase are prepared by solid phase reaction using Bi2O3, ZnO and Nb2O5 as raw material. B2O3 was introduced by liquid coating technology and solid phase mix method in the BZN ceramic specimen to reduce its sintering temperature. The effects of B2O3 doping on the sintering and dielectric properties of BZN were studied. The results show that liquid coating with B2O3 could decrease the sintering temperature of BZN ceramics from 1100°C to 900°C. The BZN ceramic composite could be sintered well at 900°C for 3 h when 0.9 mol/L H3BO3 was added and showed good dielectric properties of Εr=150, Q×f=228, τf=-362 ppm/°C.
引用
收藏
页码：1243 / 1246
相关论文
共 50 条
  • [31] Direct observation of low-temperature catalytic decomposition of H3BO3 shell in core/shell Ni/H3BO3 nanoparticles
    Zhang, X. F.
    Guan, P. F.
    Dong, X. L.
    APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING, 2012, 108 (02): : 487 - 489
  • [32] Effects of Compacting Pressure and Sintering Temperature on the Properties of Highly Porous Pure Aluminum Produced with Boric Acid (H3BO3)
    Nese O. Korpe
    N. Bașak Dürger
    Dilek Dur
    Ibrahim Celikyürek
    Powder Metallurgy and Metal Ceramics, 2021, 59 : 661 - 671
  • [33] EFFECTS OF COMPACTING PRESSURE AND SINTERING TEMPERATURE ON THE PROPERTIES OF HIGHLY POROUS PURE ALUMINUM PRODUCED WITH BORIC ACID (H3BO3)
    Korpe, Nese O.
    Durger, N. Basak
    Dur, Dilek
    Celikyurek, Ibrahim
    POWDER METALLURGY AND METAL CERAMICS, 2021, 59 (11-12) : 661 - 671
  • [34] Boric acid (H3BO3) as flux agent of clay-based ceramics, B2O3 effect in clay thermal behavior and resultant ceramics properties
    M. F. Hernández
    M. A. Violini
    M. F. Serra
    M. S. Conconi
    G. Suarez
    N. M. Rendtorff
    Journal of Thermal Analysis and Calorimetry, 2020, 139 : 1717 - 1729
  • [35] Boric acid (H3BO3) as flux agent of clay-based ceramics, B2O3 effect in clay thermal behavior and resultant ceramics properties
    Hernandez, M. F.
    Violini, M. A.
    Serra, M. F.
    Conconi, M. S.
    Suarez, G.
    Rendtorff, N. M.
    JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY, 2020, 139 (03) : 1717 - 1729
  • [36] Direct observation of low-temperature catalytic decomposition of H3BO3 shell in core/shell Ni/H3BO3 nanoparticles
    X. F. Zhang
    P. F. Guan
    X. L. Dong
    Applied Physics A, 2012, 108 : 487 - 489
  • [37] Effects of ZnO-H3BO3 addition on sintering behavior and dielectric properties of ZnO-MgO-TiO2-CaO ceramics
    Guo, Yajing
    Zhang, Yonggang
    JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2017, 28 (10) : 7248 - 7252
  • [38] Effects of ZnO-H3BO3 addition on sintering behavior and dielectric properties of ZnO-MgO-TiO2-CaO ceramics
    Yajing Guo
    Yonggang Zhang
    Journal of Materials Science: Materials in Electronics, 2017, 28 : 7248 - 7252
  • [39] Effect of Mn doping on the Structural, Dielectric, and Multiferroic Properties of BiFeO3-BaTiO3 Ceramics Fabricated by Spark Plasma Sintering
    Wang, Meng
    Xu, Zengxu
    JOURNAL OF MAGNETICS, 2022, 27 (01) : 7 - 17
  • [40] Effect of H3BO3 on the persistent luminescence and photocatalytic properties of ZnGa2O4 phosphors
    Li, Darong
    Wang, Yinhai
    Xu, Ke
    Zhao, Hui
    Hu, Zhengfa
    OPTICAL MATERIALS, 2014, 36 (11) : 1836 - 1840
12345